Formation of subsurface aluminum layers in beryllium by ion implantation and post-implant annealing
Subsurface layers of aluminum were formed in both monocrystalline and polycrystalline beryllium by implanting high doses of 200 keV Al{sup +} ions into beryllium and subsequently annealing the implanted material. Contrary to conventional wisdom on ion implantation, such layers demonstrate that ion implantation can in fact, be used, to form an essentially pure layer of an implanted species in a target material. In single crystal targets implanted at approximately 50{degree}C, aluminum layer formation was critically dependent on the implanted dose. Cross-sectional transmission electron microscopy showed the aluminium layers were monocrystalline and had abrupt interfaces with the beryllium bulk and overlayer. Scanning electron microscopy revealed defects in the layers consisting of beryllium columns extending through the aluminum from the beryllium overlayer to the bulk. Study of implanted polycrystalline material showed that layer formation occurred for all grain orientations present, but that the defect density was grain dependent. An explanation of layer formation is developed based on the observed lamellar precipitate morphology in the as-implanted state and on predicted coarsening behavior of this morphology during annealing. 41 refs., 54 figs., 2 tabs.
- Research Organization:
- Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)
- Sponsoring Organization:
- DOE/DP
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 6973485
- Report Number(s):
- UCRL-53947; ON: DE90007975
- Resource Relation:
- Other Information: Thesis (Ph.D.)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Formation of a nearly pure aluminum layer in beryllium using ion implantation
Structure of oxygen-implanted (111) silicon before and after heat-pulse annealing
Related Subjects
75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ALUMINIUM
ION IMPLANTATION
ANNEALING
BERYLLIUM
CRYSTAL STRUCTURE
INTERFACES
LAYERS
RUTHERFORD SCATTERING
SAMPLE PREPARATION
TEMPERATURE DEPENDENCE
TRANSMISSION ELECTRON MICROSCOPY
ALKALINE EARTH METALS
ELASTIC SCATTERING
ELECTRON MICROSCOPY
ELEMENTS
HEAT TREATMENTS
METALS
MICROSCOPY
SCATTERING
360101* - Metals & Alloys- Preparation & Fabrication
656003 - Condensed Matter Physics- Interactions between Beams & Condensed Matter- (1987-)