Layer-by-Layer Nanoarchitectonics of Electrochemically Active Thin Films Comprised of Radical-Containing Polymers
Abstract
Electroactive coatings based on non-conjugated redox-active polymers have increased in popularity with the development of thin film organic batteries. Here, control over coating deposition, redox-activity, and ion transport are key to improving their energy storage performance. In this work, the synthesis, solution state electrochemical characterization, and layer-by-layer (LbL) assembly of a nitroxide-based polycation and polyanion are presented. Solution state electrochemical characterization indicates that the rate of electron transfer for the nitroxide polyanion is much higher as compared to the nitroxide polycation. LbL thin films of the nitroxide polyanion and nitroxide polycation are assembled, demonstrating linear growth and tunable thickness (28 nm/layer pair). This work confirms that the ion transport mechanism of the LbL films during the redox reaction is influenced depending on the charge of the terminating layer, where the nitroxide polyanion can participate in self-doping, which leads to a contribution from cation transport. The nitroxide polyanion-terminated film also exhibits a higher capacity and a slightly reduced charge transfer resistance. However, it was also observed that a more pronounced capacity fade occurred for the polyanion-terminated film than the polycation-terminated film. Taken together, this highlights how oppositely charged radical-containing polyelectrolytes can form electroactive coatings for possible applications in energy storage ormore »
- Authors:
-
- Texas A & M Univ., College Station, TX (United States)
- Lehigh Univ., Bethlehem, PA (United States)
- Publication Date:
- Research Org.:
- Texas A & M Univ., College Station, TX (United States); Lehigh Univ., Bethlehem, PA (United States)
- Sponsoring Org.:
- USDOE Office of Science (SC), Basic Energy Sciences (BES); National Science Foundation Graduate Research Fellowship
- OSTI Identifier:
- 1871681
- Alternate Identifier(s):
- OSTI ID: 1864790; OSTI ID: 1864795
- Grant/Contract Number:
- SC0014006; FG02-05ER15720; DGE-1746932
- Resource Type:
- Accepted Manuscript
- Journal Name:
- Journal of the Electrochemical Society
- Additional Journal Information:
- Journal Volume: 169; Journal Issue: 2; Journal ID: ISSN 0013-4651
- Publisher:
- IOP Publishing
- Country of Publication:
- United States
- Language:
- English
- Subject:
- 25 ENERGY STORAGE; polymer; thin film; batteries; energy storage
Citation Formats
Easley, Alexandra D., Shaligram, Sayali V., Echols, Ian J., Nixon, Kevin, Regen, Steven L., and Lutkenhaus, Jodie L. Layer-by-Layer Nanoarchitectonics of Electrochemically Active Thin Films Comprised of Radical-Containing Polymers. United States: N. p., 2022.
Web. doi:10.1149/1945-7111/ac4cd9.
Easley, Alexandra D., Shaligram, Sayali V., Echols, Ian J., Nixon, Kevin, Regen, Steven L., & Lutkenhaus, Jodie L. Layer-by-Layer Nanoarchitectonics of Electrochemically Active Thin Films Comprised of Radical-Containing Polymers. United States. https://doi.org/10.1149/1945-7111/ac4cd9
Easley, Alexandra D., Shaligram, Sayali V., Echols, Ian J., Nixon, Kevin, Regen, Steven L., and Lutkenhaus, Jodie L. Tue .
"Layer-by-Layer Nanoarchitectonics of Electrochemically Active Thin Films Comprised of Radical-Containing Polymers". United States. https://doi.org/10.1149/1945-7111/ac4cd9. https://www.osti.gov/servlets/purl/1871681.
@article{osti_1871681,
title = {Layer-by-Layer Nanoarchitectonics of Electrochemically Active Thin Films Comprised of Radical-Containing Polymers},
author = {Easley, Alexandra D. and Shaligram, Sayali V. and Echols, Ian J. and Nixon, Kevin and Regen, Steven L. and Lutkenhaus, Jodie L.},
abstractNote = {Electroactive coatings based on non-conjugated redox-active polymers have increased in popularity with the development of thin film organic batteries. Here, control over coating deposition, redox-activity, and ion transport are key to improving their energy storage performance. In this work, the synthesis, solution state electrochemical characterization, and layer-by-layer (LbL) assembly of a nitroxide-based polycation and polyanion are presented. Solution state electrochemical characterization indicates that the rate of electron transfer for the nitroxide polyanion is much higher as compared to the nitroxide polycation. LbL thin films of the nitroxide polyanion and nitroxide polycation are assembled, demonstrating linear growth and tunable thickness (28 nm/layer pair). This work confirms that the ion transport mechanism of the LbL films during the redox reaction is influenced depending on the charge of the terminating layer, where the nitroxide polyanion can participate in self-doping, which leads to a contribution from cation transport. The nitroxide polyanion-terminated film also exhibits a higher capacity and a slightly reduced charge transfer resistance. However, it was also observed that a more pronounced capacity fade occurred for the polyanion-terminated film than the polycation-terminated film. Taken together, this highlights how oppositely charged radical-containing polyelectrolytes can form electroactive coatings for possible applications in energy storage or sensing.},
doi = {10.1149/1945-7111/ac4cd9},
journal = {Journal of the Electrochemical Society},
number = 2,
volume = 169,
place = {United States},
year = {Tue Feb 01 00:00:00 EST 2022},
month = {Tue Feb 01 00:00:00 EST 2022}
}
Works referenced in this record:
An Electroactive and Transparent Haptic Interface Utilizing Soft Elastomer Actuators with Silver Nanowire Electrodes
journal, July 2018
- Jun, Kiwoo; Kim, Jongnam; Oh, Il-Kwon
- Small, Vol. 14, Issue 35
Visible-to-NIR Electrochromic Device Prepared from a Thermally Polymerizable Electroactive Organic Monomer
journal, June 2017
- Wałęsa-Chorab, Monika; Skene, W. G.
- ACS Applied Materials & Interfaces, Vol. 9, Issue 25
There is still plenty of room for layer-by-layer assembly for constructing nanoarchitectonics-based materials and devices
journal, January 2022
- Ariga, Katsuhiko; Lvov, Yuri; Decher, Gero
- Physical Chemistry Chemical Physics, Vol. 24, Issue 7
Surface Self-Assembly of Functional Electroactive Nanofibers on Textile Yarns as a Facile Approach toward Super Flexible Energy Storage
journal, December 2017
- Tebyetekerwa, Mike; Xu, Zhen; Li, Weili
- ACS Applied Energy Materials, Vol. 1, Issue 2
Electrochemistry of Multilayer Electrodes: From the Basics to Energy Applications
journal, November 2020
- Gu, Minsu; Kim, Byeong-Su
- Accounts of Chemical Research, Vol. 54, Issue 1
Redox-active polymers: The magic key towards energy storage – a polymer design guideline progress in polymer science
journal, February 2022
- Rohland, Philip; Schröter, Erik; Nolte, Oliver
- Progress in Polymer Science, Vol. 125
The influence of current density, rest time and electrolyte composition on the self-discharge of organic radical polymers
journal, May 2021
- Gerlach, P.; Balducci, A.
- Electrochimica Acta, Vol. 377
100th Anniversary of Macromolecular Science Viewpoint: Fundamentals for the Future of Macromolecular Nitroxide Radicals
journal, February 2020
- Wang, Shaoyang; Easley, Alexandra D.; Lutkenhaus, Jodie L.
- ACS Macro Letters, Vol. 9, Issue 3
Synthesis and electrochemical behaviour of nitroxidepolymer brush thin-film electrodes for organic radical batteries
journal, January 2012
- Hung, Miao-Ken; Wang, Yu-Hsuan; Lin, Chun-Hao
- J. Mater. Chem., Vol. 22, Issue 4
Nanostructured organic radical cathodes from self-assembled nitroxide-containing block copolymer thin films
journal, January 2015
- Hauffman, G.; Vlad, A.; Janoschka, T.
- Journal of Materials Chemistry A, Vol. 3, Issue 38
Charge–Discharge with Rocking-Chair-Type Li + Migration Characteristics in a Zwitterionic Radical Copolymer Composed of TEMPO and Trifluoromethanesulfonylimide with Carbonate Electrolytes for a High-Rate Li-Ion Battery
journal, February 2017
- Tokue, Hiroshi; Murata, Tomoaki; Agatsuma, Haruka
- Macromolecules, Vol. 50, Issue 5
Polymer ionic liquid bearing radicals as an active material for organic batteries with ultrafast charge-discharge rate
journal, September 2018
- Aqil, Mohamed; Ouhib, Farid; Aqil, Abdelhafid
- European Polymer Journal, Vol. 106
Nitroxide TEMPO-containing PILs: Kinetics study and electrochemical characterizations
journal, June 2021
- Aqil, Mohamed; Aqil, Abdelhafid; Ouhib, Farid
- European Polymer Journal, Vol. 152
Solution‐Processable Thermally Crosslinked Organic Radical Polymer Battery Cathodes
journal, March 2020
- Wang, Shaoyang; Park, Albert Min Gyu; Flouda, Paraskevi
- ChemSusChem, Vol. 13, Issue 9
Charge Storage in Polymer Acid-Doped Polyaniline-Based Layer-by-Layer Electrodes
journal, October 2013
- Jeon, Ju-Won; O’Neal, Josh; Shao, Lin
- ACS Applied Materials & Interfaces, Vol. 5, Issue 20
Polyaniline nanofiber/electrochemically reduced graphene oxide layer-by-layer electrodes for electrochemical energy storage
journal, January 2015
- Jeon, Ju-Won; Kwon, Se Ra; Lutkenhaus, Jodie L.
- Journal of Materials Chemistry A, Vol. 3, Issue 7
Layer-by-Layer Assembly of Polyaniline Nanofibers and MXene Thin-Film Electrodes for Electrochemical Energy Storage
journal, November 2019
- Yun, Junyeong; Echols, Ian; Flouda, Paraskevi
- ACS Applied Materials & Interfaces, Vol. 11, Issue 51
Layer-by-layer coating of oriented conjugated polymer films towards anisotropic electronics
journal, May 2017
- Pandey, Manish; Sadakata, Shifumi; Nagamatsu, Shuichi
- Synthetic Metals, Vol. 227
High-Performance Polymer Solar Cells with Electrostatic Layer-by-Layer Self-Assembled Conjugated Polyelectrolytes as the Cathode Interlayer
journal, May 2015
- Zhang, Kai; Hu, Zhicheng; Xu, Rongguo
- Advanced Materials, Vol. 27, Issue 24
Layer-by-Layer Conjugated Extension of a Semiconducting Polymer for High-Performance Organic Field-Effect Transistor
journal, May 2015
- Jang, Mi; Kim, Se Hyun; Lee, Han-Koo
- Advanced Functional Materials, Vol. 25, Issue 25
Layer-by-layer assembly for rapid fabrication of thick polymeric films
journal, January 2012
- Li, Yang; Wang, Xu; Sun, Junqi
- Chemical Society Reviews, Vol. 41, Issue 18
Innovation in Layer-by-Layer Assembly
journal, November 2016
- Richardson, Joseph J.; Cui, Jiwei; Björnmalm, Mattias
- Chemical Reviews, Vol. 116, Issue 23
Roughness and Salt Annealing in a Polyelectrolyte Multilayer
journal, September 2013
- Ghostine, Ramy A.; Jisr, Rana M.; Lehaf, Ali
- Langmuir, Vol. 29, Issue 37
Interdiffusion in Polyelectrolyte Multilayers
journal, September 2010
- Soltwedel, Olaf; Ivanova, Oxana; Nestler, Peter
- Macromolecules, Vol. 43, Issue 17
Effect of polyelectrolyte interdiffusion on electron transport in redox-active polyelectrolyte multilayers
journal, January 2012
- Zahn, Raphael; Coullerez, Géraldine; Vörös, János
- Journal of Materials Chemistry, Vol. 22, Issue 22
Electrochemical decomposition of layer-by-layer thin films composed of TEMPO-modified poly(acrylic acid) and poly(ethyleneimine)
journal, February 2014
- Takahashi, Shigehiro; Aikawa, Yu; Kudo, Tomotaka
- Colloid and Polymer Science, Vol. 292, Issue 3
Redox Properties of Polyvinylamine- g -TEMPO in Multilayer Films with Sodium Poly(styrenesulfonate)
journal, February 2017
- Fu, Qiang; Zoudanov, Igor; Gustafsson, Emil
- ACS Applied Materials & Interfaces, Vol. 9, Issue 6
Synthesis and characterization of amorphous mesoporous silica using TEMPO-functionalized amphiphilic templates
journal, May 2016
- de Vries, Wilke; Doerenkamp, Carsten; Zeng, Zhaoyang
- Journal of Solid State Chemistry, Vol. 237
Polyelectrolyte Multilayers Studied by Electron Paramagnetic Resonance (EPR) Spin-Label Technique
journal, October 2012
- Lappan, Uwe; Wiesner, Brigitte; Zschoche, Stefan
- Applied Magnetic Resonance, Vol. 44, Issue 1-2
Diffusion-Cooperative Model for Charge Transport by Redox-Active Nonconjugated Polymers
journal, January 2018
- Sato, Kan; Ichinoi, Rieka; Mizukami, Ryusuke
- Journal of the American Chemical Society, Vol. 140, Issue 3
Relationship between Molecular Structure and Electron Transfer in a Polymeric Nitroxyl-Radical Energy Storage Material
journal, July 2014
- Kemper, Travis W.; Larsen, Ross E.; Gennett, Thomas
- The Journal of Physical Chemistry C, Vol. 118, Issue 31
Real-time insight into the doping mechanism of redox-active organic radical polymers
journal, November 2018
- Wang, Shaoyang; Li, Fei; Easley, Alexandra D.
- Nature Materials, Vol. 18, Issue 1
Electrochemical Oxidation of Amines Using a Nitroxyl Radical Catalyst and the Electroanalysis of Lidocaine
journal, December 2018
- Sato, Katsuhiko; Ono, Tetsuya; Sasano, Yusuke
- Catalysts, Vol. 8, Issue 12
Electrochemical oxidation of tertiary amines. Effect of structure upon reversibility
journal, October 1972
- Nelsen, S. F.; Hintz, P. J.
- Journal of the American Chemical Society, Vol. 94, Issue 20
Donnan Permselectivity in Layer-by-Layer Self-Assembled Redox Polyelectrolye Thin Films
journal, June 2002
- Calvo, Ernesto J.; Wolosiuk, Alejandro
- Journal of the American Chemical Society, Vol. 124, Issue 28
Odd–Even Effect on Rotational Dynamics of Spin-Labeled Polyacid Chain Segments in Polyelectrolyte Multilayers
journal, March 2019
- Lappan, Uwe; Rau, Cindy; Naas, Carolin
- Macromolecules, Vol. 52, Issue 6
Preparation of Layer-by-Layer Thin Films Composed of DNA and Ferrocene-Bearing Poly(amine)s and Their Redox Properties
journal, May 2006
- Sato, Hiroshi; Anzai, Jun-ichi
- Biomacromolecules, Vol. 7, Issue 6
Mixed Ionic and Electronic Conduction in Radical Polymers
journal, May 2020
- Yu, Ilhwan; Jeon, Daeyoung; Boudouris, Bryan
- Macromolecules, Vol. 53, Issue 11