Investigation on capacity loss mechanisms of lithium-ion pouch cells under mechanical indentation conditions
Abstract
Capacity loss was observed in Li-ion cells after mechanical deformation approaching the onset of internal short circuit (ISCr). In this paper, a series of indentation tests were carried out on commercial Li-ion cells of three capacities (500, 1500 and 2000 mAh). Both in-situ and ex-situ methods were used to investigate the mechanisms of indentation-induced capacity loss. We note after indentation test, the cell capacity reduced by 0.5%–6% of its original value. The incremental capacity (IC) analysis results showed that IC curves generally shifted to lower voltage region, indicating the increase in cell internal resistance. In addition, the fitting results of electrochemical impedance spectroscopy (EIS) indicated that mechanical indentation can result in a reduction in ohmic resistance and the increase in polarization resistance. Scanning electron microscopy (SEM) and X-ray computed tomography (XCT) results showed crushing of graphite, mud cracking of copper current collectors and enlarged pores in separator, which is proposed to be the main reasons for the increase in polarization resistance and permanent capacity loss. The rapid capacity loss due to mechanical abuse was compared with the long-term capacity fading.
- Authors:
-
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Beijing Inst. of Technology (China); Univ. of Tennessee, Knoxville, TN (United States)
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Univ. of Tennessee, Knoxville, TN (United States)
- Beijing Inst. of Technology (China)
- Publication Date:
- Research Org.:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- Sponsoring Org.:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE), Vehicle Technologies Office (EE-3V); National Natural Science Foundation of China (NSFC); China Scholarship Council (CSC)
- OSTI Identifier:
- 1619013
- Alternate Identifier(s):
- OSTI ID: 1617967
- Grant/Contract Number:
- AC05-00OR22725
- Resource Type:
- Accepted Manuscript
- Journal Name:
- Journal of Power Sources
- Additional Journal Information:
- Journal Volume: 465; Journal Issue: C; Journal ID: ISSN 0378-7753
- Publisher:
- Elsevier
- Country of Publication:
- United States
- Language:
- English
- Subject:
- 25 ENERGY STORAGE; Lithium-ion cells; Capacity loss; Mechanical indentation; Safety; Internal short circuit
Citation Formats
Zhu, Xiaoqing, Wang, Hsin, Allu, Srikanth, Gao, Yanfei, Cakmak, Ercan, Hopkins, Emma J., Veith, Gabriel M., and Wang, Zhenpo. Investigation on capacity loss mechanisms of lithium-ion pouch cells under mechanical indentation conditions. United States: N. p., 2020.
Web. doi:10.1016/j.jpowsour.2020.228314.
Zhu, Xiaoqing, Wang, Hsin, Allu, Srikanth, Gao, Yanfei, Cakmak, Ercan, Hopkins, Emma J., Veith, Gabriel M., & Wang, Zhenpo. Investigation on capacity loss mechanisms of lithium-ion pouch cells under mechanical indentation conditions. United States. https://doi.org/10.1016/j.jpowsour.2020.228314
Zhu, Xiaoqing, Wang, Hsin, Allu, Srikanth, Gao, Yanfei, Cakmak, Ercan, Hopkins, Emma J., Veith, Gabriel M., and Wang, Zhenpo. Wed .
"Investigation on capacity loss mechanisms of lithium-ion pouch cells under mechanical indentation conditions". United States. https://doi.org/10.1016/j.jpowsour.2020.228314. https://www.osti.gov/servlets/purl/1619013.
@article{osti_1619013,
title = {Investigation on capacity loss mechanisms of lithium-ion pouch cells under mechanical indentation conditions},
author = {Zhu, Xiaoqing and Wang, Hsin and Allu, Srikanth and Gao, Yanfei and Cakmak, Ercan and Hopkins, Emma J. and Veith, Gabriel M. and Wang, Zhenpo},
abstractNote = {Capacity loss was observed in Li-ion cells after mechanical deformation approaching the onset of internal short circuit (ISCr). In this paper, a series of indentation tests were carried out on commercial Li-ion cells of three capacities (500, 1500 and 2000 mAh). Both in-situ and ex-situ methods were used to investigate the mechanisms of indentation-induced capacity loss. We note after indentation test, the cell capacity reduced by 0.5%–6% of its original value. The incremental capacity (IC) analysis results showed that IC curves generally shifted to lower voltage region, indicating the increase in cell internal resistance. In addition, the fitting results of electrochemical impedance spectroscopy (EIS) indicated that mechanical indentation can result in a reduction in ohmic resistance and the increase in polarization resistance. Scanning electron microscopy (SEM) and X-ray computed tomography (XCT) results showed crushing of graphite, mud cracking of copper current collectors and enlarged pores in separator, which is proposed to be the main reasons for the increase in polarization resistance and permanent capacity loss. The rapid capacity loss due to mechanical abuse was compared with the long-term capacity fading.},
doi = {10.1016/j.jpowsour.2020.228314},
journal = {Journal of Power Sources},
number = C,
volume = 465,
place = {United States},
year = {Wed May 06 00:00:00 EDT 2020},
month = {Wed May 06 00:00:00 EDT 2020}
}
Web of Science
Works referenced in this record:
Thermal runaway mechanism of lithium ion battery for electric vehicles: A review
journal, January 2018
- Feng, Xuning; Ouyang, Minggao; Liu, Xiang
- Energy Storage Materials, Vol. 10
Thermal runaway features of large format prismatic lithium ion battery using extended volume accelerating rate calorimetry
journal, June 2014
- Feng, Xuning; Fang, Mou; He, Xiangming
- Journal of Power Sources, Vol. 255
Thermal runaway behavior during overcharge for large-format Lithium-ion batteries with different packaging patterns
journal, October 2019
- Huang, Lvwei; Zhang, Zhaosheng; Wang, Zhenpo
- Journal of Energy Storage, Vol. 25
Thermal Runaway of Lithium-Ion Batteries without Internal Short Circuit
journal, October 2018
- Liu, Xiang; Ren, Dongsheng; Hsu, Hungjen
- Joule, Vol. 2, Issue 10
Time Sequence Map for Interpreting the Thermal Runaway Mechanism of Lithium-Ion Batteries With LiNixCoyMnzO2 Cathode
journal, November 2018
- Feng, Xuning; Zheng, Siqi; He, Xiangming
- Frontiers in Energy Research, Vol. 6
Abuse by External Heating, Overcharge and Short Circuiting of Commercial Lithium-Ion Battery Cells
journal, January 2014
- Larsson, Fredrik; Mellander, Bengt-Erik
- Journal of The Electrochemical Society, Vol. 161, Issue 10
Failure mechanism of the lithium ion battery during nail penetration
journal, July 2018
- Mao, Binbin; Chen, Haodong; Cui, Zhixian
- International Journal of Heat and Mass Transfer, Vol. 122
Thermal behavior and failure mechanism of lithium ion cells during overcharge under adiabatic conditions
journal, November 2016
- Ye, Jiana; Chen, Haodong; Wang, Qingsong
- Applied Energy, Vol. 182
Abuse behavior of high-power, lithium-ion cells
journal, January 2003
- Spotnitz, R.; Franklin, J.
- Journal of Power Sources, Vol. 113, Issue 1
Combustion behavior of lithium iron phosphate battery induced by external heat radiation
journal, September 2017
- Wang, Qingsong; Huang, Peifeng; Ping, Ping
- Journal of Loss Prevention in the Process Industries, Vol. 49
Overcharge investigation of large format lithium-ion pouch cells with Li(Ni0.6Co0.2Mn0.2)O2 cathode for electric vehicles: Thermal runaway features and safety management method
journal, February 2019
- Zhu, Xiaoqing; Wang, Zhenpo; Wang, Yituo
- Energy, Vol. 169
Overcharge Investigation of Large Format Lithium-Ion Pouch Cells with Li(Ni 0.6 Co 0.2 Mn 0.2 )O 2 Cathode for Electric Vehicles: Degradation and Failure Mechanisms
journal, January 2018
- Zhu, Xiaoqing; Wang, Zhenpo; Wang, Cong
- Journal of The Electrochemical Society, Vol. 165, Issue 16
Characterization of large format lithium ion battery exposed to extremely high temperature
journal, December 2014
- Feng, Xuning; Sun, Jing; Ouyang, Minggao
- Journal of Power Sources, Vol. 272
A Comparison between Electrochemical Impedance Spectroscopy and Incremental Capacity-Differential Voltage as Li-ion Diagnostic Techniques to Identify and Quantify the Effects of Degradation Modes within Battery Management Systems
journal, August 2017
- Pastor-Fernández, Carlos; Uddin, Kotub; Chouchelamane, Gael H.
- Journal of Power Sources, Vol. 360, p. 301-318
Mechanical characterization and modeling for anodes and cathodes in lithium-ion batteries
journal, July 2018
- Wang, Lubing; Yin, Sha; Zhang, Chao
- Journal of Power Sources, Vol. 392
Mechanical integrity of 18650 lithium-ion battery module: Packing density and packing mode
journal, September 2018
- Liu, Binghe; Zhang, Jinjie; Zhang, Chao
- Engineering Failure Analysis, Vol. 91
Mechanical abuse simulation and thermal runaway risks of large-format Li-ion batteries
journal, February 2017
- Wang, Hsin; Lara-Curzio, Edgar; Rule, Evan T.
- Journal of Power Sources, Vol. 342
Failure analysis of pinch–torsion tests as a thermal runaway risk evaluation method of Li-ion cells
journal, November 2014
- Xia, Yuzhi; Li, Tianlei; Ren, Fei
- Journal of Power Sources, Vol. 265
Progressive mechanical indentation of large-format Li-ion cells
journal, February 2017
- Wang, Hsin; Kumar, Abhishek; Simunovic, Srdjan
- Journal of Power Sources, Vol. 341
Features of mechanical behavior of EV battery modules under high deformation rate
journal, October 2019
- Kalnaus, Sergiy; Wang, Hsin; Watkins, Thomas R.
- Extreme Mechanics Letters, Vol. 32
Experimental study of the impedance behavior of 18650 lithium-ion battery cells under deforming mechanical abuse
journal, December 2019
- Spielbauer, Markus; Berg, Philipp; Ringat, Michael
- Journal of Energy Storage, Vol. 26
Microscale failure mechanisms leading to internal short circuit in Li-ion batteries under complex loading scenarios
journal, July 2016
- Sahraei, Elham; Bosco, Emanuela; Dixon, Brandy
- Journal of Power Sources, Vol. 319
Direct observation of internal state of thermal runaway in lithium ion battery during nail-penetration test
journal, July 2018
- Yokoshima, Tokihiko; Mukoyama, Daikichi; Maeda, Fujio
- Journal of Power Sources, Vol. 393
Deformation and failure mechanisms of 18650 battery cells under axial compression
journal, December 2016
- Zhu, Juner; Zhang, Xiaowei; Sahraei, Elham
- Journal of Power Sources, Vol. 336
Internal configuration of prismatic lithium-ion cells at the onset of mechanically induced short circuit
journal, February 2016
- Wang, Hsin; Simunovic, Srdjan; Maleki, Hossien
- Journal of Power Sources, Vol. 306
Study of the influence of mechanical pressure on the performance and aging of Lithium-ion battery cells
journal, November 2019
- Müller, Verena; Scurtu, Rares-George; Memm, Michaela
- Journal of Power Sources, Vol. 440
Overcharge-induced capacity fading analysis for large format lithium-ion batteries with Li Ni1/3Co1/3Mn1/3O2+ Li Mn2O4 composite cathode
journal, April 2015
- Ouyang, Minggao; Ren, Dongsheng; Lu, Languang
- Journal of Power Sources, Vol. 279
Deformation and failure of lithium-ion batteries treated as a discrete layered structure
journal, October 2019
- Zhu, Juner; Li, Wei; Wierzbicki, Tomasz
- International Journal of Plasticity, Vol. 121
Investigation of the deformation mechanisms of lithium-ion battery components using in-situ micro tests
journal, August 2018
- Zhu, Juner; Zhang, Xiaowei; Luo, Hailing
- Applied Energy, Vol. 224
Internal short circuit and failure mechanisms of lithium-ion pouch cells under mechanical indentation abuse conditions:An experimental study
journal, April 2020
- Zhu, Xiaoqing; Wang, Hsin; Wang, Xue
- Journal of Power Sources, Vol. 455
Identify capacity fading mechanism in a commercial LiFePO4 cell
journal, October 2009
- Dubarry, Matthieu; Liaw, Bor Yann
- Journal of Power Sources, Vol. 194, Issue 1
A comparative study of commercial lithium ion battery cycle life in electrical vehicle: Aging mechanism identification
journal, April 2014
- Han, Xuebing; Ouyang, Minggao; Lu, Languang
- Journal of Power Sources, Vol. 251
Application of a lithium–tin reference electrode to determine electrode contributions to impedance rise in high-power lithium-ion cells
journal, October 2004
- Abraham, Daniel P.; Poppen, Steven D.; Jansen, Andrew N.
- Electrochimica Acta, Vol. 49, Issue 26
Temperature-responsive microspheres-coated separator for thermal shutdown protection of lithium ion batteries
journal, January 2015
- Ji, Weixiao; Jiang, Bolun; Ai, Fangxing
- RSC Advances, Vol. 5, Issue 1
Effects of separator breakdown on abuse response of 18650 Li-ion cells
journal, December 2007
- Roth, E. P.; Doughty, D. H.; Pile, D. L.
- Journal of Power Sources, Vol. 174, Issue 2
Synthesize battery degradation modes via a diagnostic and prognostic model
journal, December 2012
- Dubarry, Matthieu; Truchot, Cyril; Liaw, Bor Yann
- Journal of Power Sources, Vol. 219
Incremental Capacity Analysis and Close-to-Equilibrium OCV Measurements to Quantify Capacity Fade in Commercial Rechargeable Lithium Batteries
journal, January 2006
- Dubarry, Matthieu; Svoboda, Vojtech; Hwu, Ruey
- Electrochemical and Solid-State Letters, Vol. 9, Issue 10
Studies on the cycle life of commercial lithium ion batteries during rapid charge–discharge cycling
journal, December 2001
- Li, J.; Murphy, E.; Winnick, J.
- Journal of Power Sources, Vol. 102, Issue 1-2
The effect of external compressive loads on the cycle lifetime of lithium-ion pouch cells
journal, October 2017
- Barai, Anup; Tangirala, Ravichandra; Uddin, Kotub
- Journal of Energy Storage, Vol. 13
Dynamic impact tests on lithium-ion cells
journal, October 2017
- Kisters, Thomas; Sahraei, Elham; Wierzbicki, Tomasz
- International Journal of Impact Engineering, Vol. 108
Unveiling the Roles of Binder in the Mechanical Integrity of Electrodes for Lithium-Ion Batteries
journal, January 2013
- Chen, Jianchao; Liu, Jianyong; Qi, Yue
- Journal of The Electrochemical Society, Vol. 160, Issue 9
A review on the mechanical and electrical properties of graphite and modified graphite reinforced polymer composites
journal, May 2011
- Sengupta, Rajatendu; Bhattacharya, Mithun; Bandyopadhyay, S.
- Progress in Polymer Science, Vol. 36, Issue 5
Lattice model calculation of the strain energy density and other properties of crystalline LiCoO2
journal, June 1998
- Hart, F. X.; Bates, J. B.
- Journal of Applied Physics, Vol. 83, Issue 12
Nanomechanical Quantification of Elastic, Plastic, and Fracture Properties of LiCoO2
journal, May 2012
- Qu, Meng; Woodford, William H.; Maloney, John M.
- Advanced Energy Materials, Vol. 2, Issue 8
Limiting Internal Short-Circuit Damage by Electrode Partition for Impact-Tolerant Li-Ion Batteries
journal, January 2018
- Naguib, Michael; Allu, Srikanth; Simunovic, Srdjan
- Joule, Vol. 2, Issue 1