Hopping conduction and its photoquenching in molecular beam epitaxial GaAs grown at low temperatures
- Wright State Univ., Dayton, OH (United States)
As the growth temperature of molecular beam epitaxial GaAs is increased from 250 to 400{degrees}C, the dominant conduction changes from hopping conduction to band conduction with a donor activation energy of 0.65 eV. A 300{degrees}C grown layer is especially interesting because each conduction mechanism is dominant in a particular temperature range, hopping below 300K and band conduction above. Below 140K, the hopping conduction is greatly diminished (quenched) by irradiation with either infrared (hv {le} 1.12 eV) or 1.46 eV light, but then recovers above 140K with exactly the same thermal kinetics as are found for the famous EL2. Thus, the 0.65 eV donor, which is responsible for both the hopping and band conduction, is very similar to EL2, but not identical because of the different activation energy (0.65 eV vs 0.75 eV for EL2). 12 refs., 4 figs.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 535217
- Journal Information:
- Journal of Electronic Materials, Journal Name: Journal of Electronic Materials Journal Issue: 12 Vol. 22; ISSN JECMA5; ISSN 0361-5235
- Country of Publication:
- United States
- Language:
- English
Similar Records
Electrical properties of molecular beam epitaxial GaAs grown at 300-450{degrees}C
Photoquenching phenomenon enhanced by proton irradiation in semi-insulating GaAs