MOLYBDENUM ALLOY EXTRUSION DEVELOPMENT PROGRAM. Interim Technical Engineering Report No. 5, December 15, 1961-February 15, 1962
Technical Report
·
OSTI ID:4790504
Seven T''-shape extrusions of TZM were made at 3200 deg F in the evaluation of various die coating sources. Two T''-shape extrusions were made at 3200 deg F to study the effect of high-temperature solutionlng treatments on the extrudability of TZM. Severe die wssh occurred during these extrusions, resulting in poor surface quality. However, coarse macrostructure observed in the billet materlal is believed to be partially related to this poor surface quality. (auth)
- Research Organization:
- Allegheny Ludlum Steel Corp. Research Center, Brackenridge, Penna.
- NSA Number:
- NSA-16-012067
- OSTI ID:
- 4790504
- Report Number(s):
- ASD-TR-7-785(V)
- Country of Publication:
- United States
- Language:
- English
Similar Records
MOLYBDENUM ALLOY EXTRUSION DEVELOPMENT PROGRAM. Fourth Interim Technical Engineering Report, August 15, 1961-December 15, 1961
MOLYBDENUM ALLOY EXTRUSION DEVELOPMENT PROGRAM. Seventh Interim Technical Engineering and Phase III Report, June 1, 1962 to September 1, 1962
MOLYBDENUM ALLOY EXTRUSION DEVELOPMENT PROGRAM. Sixth Interim Technical Engineering Report, February 15, 1962-June 1, 1962
Technical Report
·
Sun Dec 31 23:00:00 EST 1961
·
OSTI ID:4806939
MOLYBDENUM ALLOY EXTRUSION DEVELOPMENT PROGRAM. Seventh Interim Technical Engineering and Phase III Report, June 1, 1962 to September 1, 1962
Technical Report
·
Sat Sep 01 00:00:00 EDT 1962
·
OSTI ID:4779377
MOLYBDENUM ALLOY EXTRUSION DEVELOPMENT PROGRAM. Sixth Interim Technical Engineering Report, February 15, 1962-June 1, 1962
Technical Report
·
Sun Jul 01 00:00:00 EDT 1962
·
OSTI ID:4815823