Processing-structure-property relationships in electron beam physical vapor deposited yttria stabilized zirconia coatings
Journal Article
·
· Journal of Vacuum Science and Technology. A, International Journal Devoted to Vacuum, Surfaces, and Films
- International Advanced Research Centre for Powder Metallurgy and New Materials (ARCI), Balapur (PO), Hyderabad 500 005 (India)
The physical and mechanical properties of yttria stabilized zirconia (YSZ) coatings deposited by the electron beam physical vapor deposition technique have been investigated by varying the key process variables such as vapor incidence angle and sample rotation speed. The tetragonal zirconia coatings formed under varying process conditions employed were found to have widely different surface and cross-sectional morphologies. The porosity, phase composition, planar orientation, hardness, adhesion, and surface residual stresses in the coated specimens were comprehensively evaluated to develop a correlation with the process variables. Under transverse scratch test conditions, the YSZ coatings exhibited two different crack formation modes, depending on the magnitude of residual stress. The influence of processing conditions on the coating deposition rate, column orientation angle, and adhesion strength has been established. Key relationships between porosity, hardness, and adhesion are also presented.
- OSTI ID:
- 22054027
- Journal Information:
- Journal of Vacuum Science and Technology. A, International Journal Devoted to Vacuum, Surfaces, and Films, Journal Name: Journal of Vacuum Science and Technology. A, International Journal Devoted to Vacuum, Surfaces, and Films Journal Issue: 3 Vol. 29; ISSN 1553-1813
- Country of Publication:
- United States
- Language:
- English
Similar Records
Nucleation of epitaxial yttria-stabilized zirconia on biaxially textured (001) Ni for deposited conductors
MOCVD of yttria stabilized zirconia on Co-Cr
Characterization of yttria-stabilized zirconia coatings with controlled nanometer-sized porosity by SANS.
Journal Article
·
Mon Apr 24 00:00:00 EDT 2000
· Applied Physics Letters
·
OSTI ID:20216001
MOCVD of yttria stabilized zirconia on Co-Cr
Conference
·
Tue Aug 01 00:00:00 EDT 1995
·
OSTI ID:82554
Characterization of yttria-stabilized zirconia coatings with controlled nanometer-sized porosity by SANS.
Conference
·
Sat Nov 30 23:00:00 EST 2002
· Appl. Phys. A
·
OSTI ID:925011