Nickel aluminide alloys with improved weldability
Patent
·
OSTI ID:869874
- Knoxville, TN
- Lenior City, TN
Weldable nickel aluminide alloys which are essentially free, if not entirely free, of weld hot cracking are provided by employing zirconium concentrations in these alloys of greater than 2.6 wt. % or sufficient to provide a substantial presence of Ni--Zr eutectic phase in the weld so as to prevent weld hot cracking. Weld filler metals formed from these so modified nickel aluminide alloys provide for crack-free welds in previously known nickel aluminide alloys.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- DOE Contract Number:
- AC05-84OR21400
- Assignee:
- Martin Marietta Energy Systems, Inc. (Oak Ridge, TN)
- Patent Number(s):
- US 5413876
- Application Number:
- 07/970,757
- OSTI ID:
- 869874
- Country of Publication:
- United States
- Language:
- English
Nickel Aluminides for Structural Use
|
journal | May 1986 |
Similar Records
Nickel aluminide alloys with improved weldability
Analysis of weld solidification cracking in cast nickel aluminide alloys
Welding studies of nickel aluminide and nickel-iron aluminides
Patent
·
Tue May 09 00:00:00 EDT 1995
·
OSTI ID:869874
Analysis of weld solidification cracking in cast nickel aluminide alloys
Technical Report
·
Fri Sep 01 00:00:00 EDT 1995
·
OSTI ID:869874
Welding studies of nickel aluminide and nickel-iron aluminides
Technical Report
·
Thu Aug 01 00:00:00 EDT 1985
·
OSTI ID:869874
+2 more
Related Subjects
nickel
aluminide
alloys
improved
weldability
weldable
essentially
free
entirely
weld
hot
cracking
provided
employing
zirconium
concentrations
wt
sufficient
provide
substantial
presence
ni-zr
eutectic
phase
prevent
filler
metals
formed
modified
crack-free
welds
previously
essentially free
weld filler
nickel aluminide
aluminide alloys
aluminide alloy
filler metal
hot cracking
improved weldability
filler metals
modified nickel
/428/148/228/420/
aluminide
alloys
improved
weldability
weldable
essentially
free
entirely
weld
hot
cracking
provided
employing
zirconium
concentrations
wt
sufficient
provide
substantial
presence
ni-zr
eutectic
phase
prevent
filler
metals
formed
modified
crack-free
welds
previously
essentially free
weld filler
nickel aluminide
aluminide alloys
aluminide alloy
filler metal
hot cracking
improved weldability
filler metals
modified nickel
/428/148/228/420/