Correlation of the Structure with Performance in MEH-PPV/dPS Thin Films Illuminated during Processing
- Univ. of Tennessee, Knoxville, TN (United States)
- Rice Univ., Houston, TX (United States). SIMS Lab.
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)
Thin films containing conjugated polymers have been used in a wide array of optoelectronic devices, and much research has focused on the conformation of the conjugated polymer as a key aspect to tuning the performance of the resulting devices. White light exposure has been studied as a post-processing method to alter the film’s morphology and photoluminescence (PL) in systems composed of poly[2-methoxy-5-(2-ethylhexyloxy)-1,4-phenylenevinylene] (MEH-PPV) and polystyrene (PS). To date, there have been few studies that correlate the changes in the depth profile with the PL performance of MEH-PPV/PS films. This study is designed to address this gap in knowledge. Thin films of MEH-PPV/dPS annealed above the glass transition temperatures (Tg) in an illuminated environment led to lower PL than that found in annealed samples that are not illuminated. However, at higher MEH-PPV loading in the blend film, the extent of variation of PL with illumination diminished. Additionally, time-of-flight secondary ion mass spectrometry and small-angle neutron scattering document the three-dimensional morphology of the films under illumination conditions, which are correlated with the changes in PL. Illumination during annealing compressed MEH-PPV-rich layers in the thin film blends at low loadings of MEH-PPV (below 10 wt %) but resulted in significant in-plane phase separation at higher loadings (above 15 wt %). Both changes increase interchain interactions and lower the PL of the illuminated samples. The changes in the depth profile significantly alter the PL of the films, while the in-plane phase separation affected the optoelectronic properties to a lesser degree. This work, therefore, provides insights into how illumination and film composition can be utilized to predictably alter the structure and optoelectronic performance of conjugated polymer blend films.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES); National Science Foundation (NSF)
- Grant/Contract Number:
- AC05-00OR22725; DMR-1808946; CBET-1626418
- OSTI ID:
- 1844892
- Journal Information:
- ACS Applied Polymer Materials, Vol. 3, Issue 8; ISSN 2637-6105
- Publisher:
- ACS PublicationsCopyright Statement
- Country of Publication:
- United States
- Language:
- English
Similar Records
Hybrid device based on GaN nanoneedles and MEH-PPV/PEDOT:PSS polymer
Investigation of electrical and optical properties of MEH-PPV: ZnO nanocomposite films for OLED applications