Thermal-Mechanical Elastic-Plastic and Ductile Failure Model Calibrations for 6061-T651 Aluminum Alloy from Plate
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)
Numerical simulations of metallic structures undergoing rapid loading into the plastic range require material models that accurately represent the response. In general, the material response can be seen as having four interrelated parts: the baseline response under slow loading, the effect of strain rate, the conversion of plastic work into heat and the effect of temperature. In essence, the material behaves in a thermal-mechanical manner if the loading is fast enough so when heat is generated by plastic deformation it raises the temperature and therefore influences the mechanical response. In these cases, appropriate models that can capture the aspects listed above are necessary. The matters of interest here are the elastic-plastic response and ductile failure behavior of 6061-T651 aluminum alloy under the conditions described above. The work was accomplished by first designing and conducting a material test program to provide data for the calibration of a modular $$J_2$$ plasticity model with isotropic hardening as well as a ductile failure model. Both included modules that accounted for temperature and strain rate dependence. The models were coupled with an adiabatic heating module to calculate the temperature rise due to the conversion of plastic work to heat. The test program included uniaxial tension tests conducted at room temperature, 150 and 300 C and at strain rates between 10–4 and 103 1/s as well as four geometries of notched tension specimens and two tests on specimens with shear-dominated deformations. The test data collected allowed the calibration of both the plasticity and the ductile failure models. Most test specimens were extracted from a single piece of plate to maintain consistency. Notched tension tests came from a possibly different plate, but from the same lot. When using the model in structural finite element calculations, element formulations and sizes different from those used to model the test specimens in the calibration are likely to be used. A brief investigation demonstrated that the failure model can be particularly sensitive to the element selection and provided an initial guide to compensate in a specific example.
- Research Organization:
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)
- Sponsoring Organization:
- USDOE National Nuclear Security Administration (NNSA)
- DOE Contract Number:
- AC04-94AL85000; NA0003525
- OSTI ID:
- 1772885
- Report Number(s):
- SAND2021-2983; 694951
- Country of Publication:
- United States
- Language:
- English