Thermal-Mechanical Elastic-Plastic and Ductile Failure Model Calibrations for 304L Stainless Steel Alloy

Technical Report · Mon Feb 01 04:00:00 EST 2021

DOI:https://doi.org/10.2172/1769256· OSTI ID:1769256

Corona, Edmundo ^[1]; Kramer, Sharlotte Lorraine Bolyard ^[1]; Lester, Brian T. ^[1]; Jones, Amanda R. ^[1]; Sanborn, Brett ^[1]; Shand, Lyndsay ^[1]; Fietek, Carter John ^[1]

---

1. Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)

Numerical simulations of metallic structures undergoing rapid loading into the plastic range require material models that accurately represent the response. In general, the material response can be seen as having four interrelated parts: the baseline response under slow loading, the effect of strain rate, the conversion of plastic work into heat and the effect of temperature. In essence, the material behaves in a thermal-mechanical manner if the loading is fast enough so when heat is generated by plastic deformation it raises the temperature and therefore influences the mechanical response. In these cases, appropriate models that can capture the aspects listed above are necessary. The material of interest here is 304L stainless steel, and the objective of this work is to calibrate thermal-mechanical models: one for the constitutive behavior and another for failure. The work was accomplished by first designing and conducting a material test program to provide data for the calibration of the models. The test program included uniaxial tension tests conducted at room temperature, 150 and 300 C and at strain rates between 10^–4 and 10³ 1/s. It also included notched tension and shear-dominated compression hat tests specifically designed to calibrate the failure model. All test specimens were extracted from a single piece of plate to maintain consistency. The constitutive model adopted was a modular $$J_2$$ plasticity model with isotropic hardening that included rate and temperature dependence. A criterion for failure initiation based on a critical value of equivalent plastic strain fitted the failure data appropriately and was adopted. Possible ranges of the values of the parameters of the models were determined partially on historical data from calibrations of the same alloy from other lots and are given here. The calibration of the parameters of the models were based on finite element simulations of the various material tests using relatively ne meshes and hexahedral elements. When using the model in structural finite element calculations, however, element formulations and sizes different from those in the calibration are likely to be used. A brief investigation demonstrated that the failure initiation predictions can be particularly sensitive to the element selection and provided an initial guide to compensate for the effect of element size in a specific example.

• Research Organization: Sandia National Laboratories (SNL-NM), Albuquerque, NM (United States)
• Sponsoring Organization: USDOE National Nuclear Security Administration (NNSA)
• DOE Contract Number: AC04-94AL85000; NA0003525
• OSTI ID: 1769256
• Report Number(s): SAND2021-1752; 694236
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE