Study of the Effect of Swelling on Irradiation Assisted Stress Corrosion Cracking
- Idaho National Lab. (INL), Idaho Falls, ID (United States)
This report describes the methodology used to study the effect of swelling on the crack growth rate of an irradiation-assisted stress corrosion crack that is propagating in highly irradiated stainless steel 304 material irradiated to 33 dpa in the Experimental Breeder Reactor-II. The material selection, specimens design, experimental apparatus and processes are described. The results of the current test are presented.
- Research Organization:
- Idaho National Lab. (INL), Idaho Falls, ID (United States)
- Sponsoring Organization:
- USDOE Office of Nuclear Energy (NE)
- DOE Contract Number:
- AC07-05ID14517
- OSTI ID:
- 1364496
- Report Number(s):
- INL/EXT-16-39932; M3LW-15IN0402162; TRN: US1703392
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of Swelling on Irradiation-Assisted Stress Corrosion Cracking
Irradiation Assisted Stress Corrosion Cracking of Austenitic Stainless Steel in BWR Conditions
Irradiation-assisted stress corrosion cracking behavior of austenitic stainless steels applicable to LWR core internals.
Technical Report
·
Sat Jul 01 00:00:00 EDT 2017
·
OSTI ID:1364496
Irradiation Assisted Stress Corrosion Cracking of Austenitic Stainless Steel in BWR Conditions
Technical Report
·
Mon Jun 26 00:00:00 EDT 2017
·
OSTI ID:1364496
Irradiation-assisted stress corrosion cracking behavior of austenitic stainless steels applicable to LWR core internals.
Technical Report
·
Tue Jan 31 00:00:00 EST 2006
·
OSTI ID:1364496