Irradiation Assisted Stress Corrosion Cracking of Austenitic Stainless Steel in BWR Conditions
- Idaho National Lab. (INL), Idaho Falls, ID (United States). Nuclear Science User Facilities (NSUF)
As a first step toward full scale utilization of the Advanced Test Reactor (ATR) and associated post irradiation examination (PIE) equipment at INL, the NRC and INL staffs have formulated a test program that is designed to help to establish INL and the Nuclear Science User Facilities (NSUF) as a viable destination for irradiation and PIE of reactor structural materials. This initial research program utilized two materials (304 Stainless Steel weld Heat Affected Zone (HAZ) and sensitized 304L stainless steel) that have previously been irradiated at the Halden reactor in Norway and tested at Argonne National Laboratory (ANL) so that test results may be compared, thereby establishing a measure of comparability between Halden and ATR irradiations. A secondary objective of this test program was to characterize the quality of data produced using INL’s newly constructed irradiation assisted stress corrosion cracking (IASCC) test cells. The specimens were be tested in typical boiling water reactor (BWR) conditions to measure stress corrosion cracking (SCC) and fracture toughness of un-irradiated specimens and then IASCC and fracture toughness of specimens irradiated to a fluence equal to approximately 1.0 X 1021 n/cm2 (E > 1 MeV).
- Research Organization:
- Idaho National Laboratory, Idaho Falls, ID (United States)
- Sponsoring Organization:
- USDOE Office of Nuclear Energy (NE); USNRC
- DOE Contract Number:
- AC07-05ID14517
- OSTI ID:
- 1408502
- Report Number(s):
- INL/EXT--17-42276
- Country of Publication:
- United States
- Language:
- English
Similar Records
Irradiation-Assisted Stress Corrosion Cracking of Austenitic Stainless Steels in BWR Environments
Baseline Fracture Toughness and SCC Testing of Alloys X750 and XM-19 (Phase I)
Baseline Fracture Toughness and CGR testing of alloys X-750 and XM-19 (EPRI Phase I)
Technical Report
·
Tue Jun 01 00:00:00 EDT 2010
·
OSTI ID:1224951
Baseline Fracture Toughness and SCC Testing of Alloys X750 and XM-19 (Phase I)
Technical Report
·
Tue Feb 28 23:00:00 EST 2012
·
OSTI ID:1035808
Baseline Fracture Toughness and CGR testing of alloys X-750 and XM-19 (EPRI Phase I)
Technical Report
·
Mon Oct 01 00:00:00 EDT 2012
·
OSTI ID:1060986