Insights from incorporating reference electrodes in symmetric lithium-ion cells with layered oxide or graphite electrodes
Abstract
Symmetric cells provide complementary means to probe electrochemical processes in lithium-ion batteries. Here, positive and negative electrodes harvested from conventional oxide/graphite cells are cross-paired, and the assembled reference-electrode-bearing symmetric cells are cycled/aged. For graphite symmetric cells, the electrode potentials and impedances remain nearly constant during calendar aging and the parasitic currents are typically small. However, at higher cell voltages when the “positive” graphite potential exceeds 1.0 V vs. Li/Li+, the capacity loss is higher, indicating that even a mild (but prolonged) overdischarge can damage the SEI. For the layered-oxide symmetric cells there are strong parasitic currents and a persistent slide of the electrode potential over time during calendar aging. Significant cell impedance rise, especially at higher hold voltages, is also observed. Curiously, the impedance rise in the “negative” oxide electrode, which experiences potentials below 4.0 V vs. Li/Li+, is greater than in the “positive” oxide electrode that experiences much higher potentials. We postulate that electrolyte oxidation is responsible for the behavior of these oxide symmetric cells, as it supplies electrons (that bind more Li+ into the cathode, causing the potential slide) and protons (that contribute to impedance rise). Furthermore, these insights can guide the development of future lithium-ion cell chemistries.
- Authors:
-
- Argonne National Lab. (ANL), Lemont, IL (United States)
- Publication Date:
- Research Org.:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Org.:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE), Vehicle Technologies Office (EE-3V); USDOE
- OSTI Identifier:
- 1558784
- Alternate Identifier(s):
- OSTI ID: 1558745
- Grant/Contract Number:
- AC02-06CH11357
- Resource Type:
- Accepted Manuscript
- Journal Name:
- Journal of Power Sources
- Additional Journal Information:
- Journal Volume: 438; Journal Issue: C; Journal ID: ISSN 0378-7753
- Publisher:
- Elsevier
- Country of Publication:
- United States
- Language:
- English
- Subject:
- 25 ENERGY STORAGE; calendar-aging; capacity gain; electrolyte oxidation; impedance rise; potential slide
Citation Formats
Kalaga, Kaushik, Rodrigues, Marco-Tulio F., Bareño, Javier, Shkrob, Ilya A., and Abraham, Daniel P. Insights from incorporating reference electrodes in symmetric lithium-ion cells with layered oxide or graphite electrodes. United States: N. p., 2019.
Web. doi:10.1016/j.jpowsour.2019.227033.
Kalaga, Kaushik, Rodrigues, Marco-Tulio F., Bareño, Javier, Shkrob, Ilya A., & Abraham, Daniel P. Insights from incorporating reference electrodes in symmetric lithium-ion cells with layered oxide or graphite electrodes. United States. https://doi.org/10.1016/j.jpowsour.2019.227033
Kalaga, Kaushik, Rodrigues, Marco-Tulio F., Bareño, Javier, Shkrob, Ilya A., and Abraham, Daniel P. Mon .
"Insights from incorporating reference electrodes in symmetric lithium-ion cells with layered oxide or graphite electrodes". United States. https://doi.org/10.1016/j.jpowsour.2019.227033. https://www.osti.gov/servlets/purl/1558784.
@article{osti_1558784,
title = {Insights from incorporating reference electrodes in symmetric lithium-ion cells with layered oxide or graphite electrodes},
author = {Kalaga, Kaushik and Rodrigues, Marco-Tulio F. and Bareño, Javier and Shkrob, Ilya A. and Abraham, Daniel P.},
abstractNote = {Symmetric cells provide complementary means to probe electrochemical processes in lithium-ion batteries. Here, positive and negative electrodes harvested from conventional oxide/graphite cells are cross-paired, and the assembled reference-electrode-bearing symmetric cells are cycled/aged. For graphite symmetric cells, the electrode potentials and impedances remain nearly constant during calendar aging and the parasitic currents are typically small. However, at higher cell voltages when the “positive” graphite potential exceeds 1.0 V vs. Li/Li+, the capacity loss is higher, indicating that even a mild (but prolonged) overdischarge can damage the SEI. For the layered-oxide symmetric cells there are strong parasitic currents and a persistent slide of the electrode potential over time during calendar aging. Significant cell impedance rise, especially at higher hold voltages, is also observed. Curiously, the impedance rise in the “negative” oxide electrode, which experiences potentials below 4.0 V vs. Li/Li+, is greater than in the “positive” oxide electrode that experiences much higher potentials. We postulate that electrolyte oxidation is responsible for the behavior of these oxide symmetric cells, as it supplies electrons (that bind more Li+ into the cathode, causing the potential slide) and protons (that contribute to impedance rise). Furthermore, these insights can guide the development of future lithium-ion cell chemistries.},
doi = {10.1016/j.jpowsour.2019.227033},
journal = {Journal of Power Sources},
number = C,
volume = 438,
place = {United States},
year = {Mon Aug 26 00:00:00 EDT 2019},
month = {Mon Aug 26 00:00:00 EDT 2019}
}
Web of Science