Band Edge Traps at Spectroscopically-Detected O-Atom Vacancies in Nanocrystalline Zro (2) And Hfo (2) : An Engineering Solution for Elimination of O-Atom Vacancy Defects in Non-Crystalline Ternary Silicate Alloys
Journal Article
·
· ECS Trans.1:381,2006
OSTI ID:913044
Spectroscopic studies, supported by theory indicate that neutral and negatively charged O-atom vacancies are the most important intrinsic defects in nanocrystalline thin films of Hf(Zr)O2. O-atom vacancy defects are identified in this paper by different spectroscopic technique: vacuum ultra-violet spectroscopic ellipsometry, near edge x-ray absorption spectroscopy, and cathodo-luminescence spectroscopy. O-vacancy defects are active as (1) interface traps for Si substrate injection of holes, and (2) bulk film traps for Si substrate injection of electrons. The markedly different electron and hole trapping properties are a potentially serious problem for threshold voltage control and stability in CMOS inverter FETs using nanocrystalline Hf(Zr)O2 dielectrics. O-vacancy defects are not observed spectroscopically in thermally and chemically stable Zr Si oxynitride alloy films, (SiO2)x(Si3N4)y(ZrO2)z, that have been annealed at 1100 C in Ar. Si3N4 concentrations in these alloys must be controlled within narrow limits, {approx}0.36 to 0.4, with equal SiO2 and ZrO2 concentrations of approximately 0.32 to 0.3.
- Research Organization:
- Stanford Linear Accelerator Center (SLAC)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC02-76SF00515
- OSTI ID:
- 913044
- Report Number(s):
- SLAC-REPRINT-2006-325
- Journal Information:
- ECS Trans.1:381,2006, Journal Name: ECS Trans.1:381,2006 Journal Issue: 5 Vol. 1
- Country of Publication:
- United States
- Language:
- English
Similar Records
Spectroscopic Studies of O-Vacancy Defects in Transition Metal Oxides
Spectroscopic Studies of Electronically Active Defects in Transition Metal Oxides for Advanced Si Devices
Interfacial Transition Regions at Germanium/Hf Oxide Based Dielectric Interfaces: Qualitative Differences Between Non-Crystalline Hf Si Oxynitride and Nanocrystalline HfO2 Gate Stacks
Journal Article
·
Wed Jun 03 00:00:00 EDT 2009
· J. Mater. Sci. Mater. Electron 18:S263,2007
·
OSTI ID:953941
Spectroscopic Studies of Electronically Active Defects in Transition Metal Oxides for Advanced Si Devices
Conference
·
Thu Jun 04 00:00:00 EDT 2009
· AIP Conf.Proc.882:364,2007
·
OSTI ID:953926
Interfacial Transition Regions at Germanium/Hf Oxide Based Dielectric Interfaces: Qualitative Differences Between Non-Crystalline Hf Si Oxynitride and Nanocrystalline HfO2 Gate Stacks
Journal Article
·
Wed Dec 31 23:00:00 EST 2008
· Microelectronic Engineering
·
OSTI ID:980283