Influence of Annealing Conditions on Dopant Antirotation of Si+ and Mg+ Implanted GaN
- ORNL
This report reflects the results of heat treatment under various conditions on as-grown and ion implanted GaN. The PL spectrums of as-grown GaN and GaN with 400 A AlN cap were almost identical. This fact allows one to use PL analysis without AlN stripping. As-grown GaN and ion implanted with Mg and Si crystals were annealed at 1300 C for 10 minutes in three different conditions: in flowing argon gas; in flowing ultra high purity nitrogen; and in a quartz capsule sealed with nitrogen gas. The results of PL, RBS, SEM and TEM analysis show an advantage of GaN high temperature annealing in quartz capsules with nitrogen ambient as compared to annealing in argon and nitrogen gas flow. Encapsulation with nitrogen over-pressure prevents the decomposition of the GaN crystal and the AlN capping film, and allows one to achieve optical activation of implanted Mg and Si after 1300 C annealing.
- Research Organization:
- Oak Ridge National Lab., TN (US)
- Sponsoring Organization:
- USDOE Office of Science (US)
- DOE Contract Number:
- AC05-00OR22725
- OSTI ID:
- 755643
- Report Number(s):
- ORNL/CP-105487
- Country of Publication:
- United States
- Language:
- English
Similar Records
High-temperature annealing and optical activation of Eu-implanted GaN
Doping of GaN by ion implantation: Does It Work?