Diffusion-induced grain boundary migration during ion beam mixing of Au/Cu bilayers
Experiments were performed to evaluate the effect of 1.5 MeV Kr irradiation on diffusion-induced grain boundary migration (DIGM) in Au/Cu bilayers in the temperature range of 300{le}T{le}050K. The experimental results were consistent with DIGM occurring in bilayers both during irradiation and during annealing treatments. Rutherford backscattering spectrometry showed a nearly uniform distribution of Cu present through the entire thickness of appropriately prepared polycrystalline Au films irradiated or annealed at temperatures {ge}400K. No parallel effect was seen in similarly treated single-crystal films. In each polycrystalline sample studied, irradiation resulted in greater amounts of Cu present uniformly in the Au compared to annealing-only. The magnitudes of measured Cu compositions were substantially greater than that expected solely from grain boundary diffusion. A simple analysis of the process indicated that ion irradiation affects DIGM by increasing the composition of Cu present in alloyed zones and/or by increasing the grain boundary velocity in the Au.
- Research Organization:
- Argonne National Lab., IL (United States)
- Sponsoring Organization:
- USDOE; USDOE, Washington, DC (United States)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 7059400
- Report Number(s):
- ANL/CP-76009; CONF-9209200-4; ON: DE93000508
- Resource Relation:
- Conference: 8. international conference on ion beam modification of materials, Heidelberg (Germany), 7-11 Sep 1992
- Country of Publication:
- United States
- Language:
- English
Similar Records
Interdiffusion and grain-boundary migration in Au-Cu bilayers during ion-irradiation
Interdiffusion and grain-boundary migration in Au-Cu bilayers during ion-irradiation
Related Subjects
36 MATERIALS SCIENCE
COPPER
MIXING
RADIATION EFFECTS
GOLD
ANNEALING
BACKSCATTERING
DIFFUSION
FILMS
GRAIN BOUNDARIES
ION BEAMS
KRYPTON IONS
LAYERS
MEV RANGE 01-10
POLYCRYSTALS
RUTHERFORD SCATTERING
TEMPERATURE RANGE 0273-0400 K
TEMPERATURE RANGE 0400-1000 K
THICKNESS
BEAMS
CHARGED PARTICLES
CRYSTAL STRUCTURE
CRYSTALS
DIMENSIONS
ELASTIC SCATTERING
ELEMENTS
ENERGY RANGE
HEAT TREATMENTS
IONS
METALS
MEV RANGE
MICROSTRUCTURE
SCATTERING
TEMPERATURE RANGE
TRANSITION ELEMENTS
070205* - Radiation Sources- Industrial Applications
Radiation Processing- (1987-)
360106 - Metals & Alloys- Radiation Effects