Identifying Electronic Properties Relevant to Improving Stability in a-Si:H-Based Cells and Overall Performance in a-Si,Ge:H-Based Cells; final Subcontract Report, 18 April 1994-15 January 1998
- Department of Physics and Materials Science Institute, University of Oregon
The work carried out by the University of Oregon Under this subcontract focused on the characterization and evaluation of low-gap (a-Si,Ge:H) alloy materials and on issues related to overall stability in the mid-gap (a-SiH) materials. First, researchers characterized an extensive series of Uni-Solar a-Si,Ge:H samples using drive-level capacitance profiling and the analysis of sub-band-gap photocapacitance and photocurrent spectra. Thus, several bands of deep defect transitions were identified. Researchers were able to verify that charged defects are responsible for the different observed defect bands in device-quality a-Si,Ge:H alloy material. Second, they reported results of their measurements on a-Si,Ge:H alloy ''cathodic'' samples produced at Harvard University; these samples were found to exhibit significantly lower defect densities in the high Ge composition range (>50at.% Ge) than alloy samples produced either by conventional glow discharge of photo-chemical vapor deposition. Third, they performed voltage pulse stimulated capacitance transient measurements on a-Si:H/a-Si,Ge:H heterostructure samples to look for carrier trapping states that might be associated with this interface; they found there was a clear signature of trapped hole emission extending over long times associated specifically with the interface itself in concentrations of roughly 10{sup 11} cm{sup -2}. Fourth, researchers reported the results on several hot-wire a-Si:H samples produced with varying hydrogen levels. Their studies indicate that hot-wire-produced a-Si:H, with H levels between 2-5at.%, should lead to mid-gap devices with superior properties. Finally, they discussed some results on glow-discharge material, as well electron-cyclotron-resonance-deposited a-Si:H grown under hydrogen dilution conditions, and confirmed that, in terms of deep-defect creation, such films exhibited improved stability compared to conventional glow-discharge material.
- Research Organization:
- National Renewable Energy Lab., Golden, CO (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- AC36-99GO10337
- OSTI ID:
- 6699
- Report Number(s):
- NREL/SR-520-25802; ON: DE00006699
- Country of Publication:
- United States
- Language:
- English
Similar Records
Identifying electronic properties relevant to improving stability in a-Si:H-based cells and overall performance in a-Si,Ge:H-based cells. Annual subcontract report, April 18, 1994--April 17, 1995
Microscopic Origins of Metastable Effects in a-Si:H and Deep Defect Characterization in a-Si,Ge:H Alloys, Annual Subcontract Report, 1 February 1992 - 31 January 1993
Identifying electronic properties relevant to improving stability in a-Si:H-based cells and overall performance in a-Si,Ge:H-based cells. Annual subcontract report, 18 April 1995--17 April 1996
Technical Report
·
Tue Oct 31 23:00:00 EST 1995
·
OSTI ID:132673
Microscopic Origins of Metastable Effects in a-Si:H and Deep Defect Characterization in a-Si,Ge:H Alloys, Annual Subcontract Report, 1 February 1992 - 31 January 1993
Technical Report
·
Sun Aug 01 00:00:00 EDT 1993
·
OSTI ID:10180625
Identifying electronic properties relevant to improving stability in a-Si:H-based cells and overall performance in a-Si,Ge:H-based cells. Annual subcontract report, 18 April 1995--17 April 1996
Technical Report
·
Fri Feb 28 23:00:00 EST 1997
·
OSTI ID:459363