Low-energy excitations in amorphous films of silicon and germanium
- Laboratory of Atomic and Solid State Physics, Cornell University, Ithaca, New York 14853-2501 (United States)
We present measurements of internal friction and shear modulus of amorphous Si (a-Si) and amorphous Ge (a-Ge) films on double-paddle oscillators at 5500 Hz from 0.5 K up to room temperature. The temperature- independent plateau in internal friction below 10 K, which is common to all amorphous solids, also exists in these films. However, its magnitude is smaller than found for all other amorphous solids studied to date. Furthermore, it depends critically on the deposition methods. For a-Si films, it decreases in the sequence of electron-beam evaporation, sputtering, self-ion implantation, and hot-wire chemical-vapor deposition (HWCVD). Annealing can also reduce the internal friction of the amorphous films considerably. Hydrogenated a-Si with 1 at.{percent} H prepared by HWCVD leads to an internal friction more than two orders of magnitude smaller than observed for all other amorphous solids. The internal friction increases after the hydrogen is removed by effusion. Our results are compared with earlier measurements on a-Si and a-Ge films, none of which had the sensitivity achieved here. The variability of the low-energy tunneling states in the a-Si and a-Ge films may be a consequence of the tetrahedrally bonded covalent continuous random network. The perfection of this network, however, depends critically on the preparation conditions, with hydrogen incorporation playing a particularly important role. {copyright} {ital 1998} {ital The American Physical Society}
- OSTI ID:
- 659330
- Journal Information:
- Physical Review, B: Condensed Matter, Journal Name: Physical Review, B: Condensed Matter Journal Issue: 14 Vol. 58; ISSN 0163-1829; ISSN PRBMDO
- Country of Publication:
- United States
- Language:
- English
Similar Records
Amorphous Solid without Low Energy Excitations
New results on the microstructure of amorphous silicon as observed by internal friction