Damage behaviour and annealing of germanium implanted 6H-SiC
- Forschungszentrum Rossendorf, Dresden (Germany); and others
The present paper reports a study of the defect reduction and recrystallisation during annealing of Ge{sup +}-implanted 6H-SiC. Implants have been performed at 200 keV with doses of 1{times}10{sup 14} and 1{times}10{sup 15} cm. Furnace annealing has been carried out at temperatures of 500{degrees}, 950{degrees} and 1500{degrees}C. Several analytical techniques including Rutherford backscattering spectrometry in conjunction with channeling (RBS/C), cross-sectional transmission electron microscopy (XTEM), positron annihilation spectroscopy (PAS), Raman Scattering (RS), and Electron Paramagnetic Resonance (EPR) measurements have been employed for sample characterisation. It has been shown that damage removal is more complicated than in ion-implanted Si. Using PAS deeply diffusing vacancy-like defects were found far below the region defined by TRIM as containing the maximum amount of nuclear energy deposition. The amorphised SiC is characterised by carbon dangling bonds as revealed by EPR. The recrystallisation of amorphised SiC layers has been found to be unsatisfactory for temperatures up to 1500{degrees}C. The use of ion-beam-induced epitaxial crystallisation (IBIEC) has been more successful as lattice regrowth, although still imperfect, has been observed to occur at a temperature as low as 500{degrees}C.
- OSTI ID:
- 621317
- Report Number(s):
- CONF-9606110-; CNN: Contract ERBCHRX-CT93-0125; TRN: 98:002114-0060
- Resource Relation:
- Conference: 11. international conference on ion implantation technology, Austin, TX (United States), 17-21 Jun 1996; Other Information: PBD: 1996; Related Information: Is Part Of Ion implantation technology - 96; Ishida, E.; Banerjee, S.; Mehta, S. [eds.] [and others]; PB: 859 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Compensation implants in 6H{endash}SiC
Silicon nitride fibres synthesised by a gas-phase process