Oxidation resistance of sputtered Ni{sub 3}(AlCr) nanocrystalline coating

Journal Article · Tue Apr 01 04:00:00 EST 1997 · Oxidation of Metals

DOI:https://doi.org/10.1007/BF01668513· OSTI ID:518357

Wang, Fuhui ^[1]

---

1. Inst. of Corrosion and Protection of Metals, Shenyang (China)

Isothermal and cyclic oxidation resistance at 1000{degrees}C in air were investigated for a cast Cr-containing Ni{sub 3}Al-base alloy and its sputtered nanocrystalline coating. The results indicated that both the cast Ni{sub 3}Al alloy and its sputtered coating exhibit excellent isothermal oxidation resistance as a result of the formation of Al{sub 2}O{sub 3} scales. However, the cast alloy possesses very poor cyclic oxidation resistance because of the spallation of the initially formed Al{sub 2}O{sub 3} scale during cooling and subsequent formation of NiO. On the contrary, the sputtered Ni{sub 3}(AlCr) nanocrystalline coating exhibits very good cyclic oxidation resistance due to the significant improvement of the adhesion of Al{sub 2}O{sub 3}.

• Sponsoring Organization: USDOE
• OSTI ID: 518357
• Journal Information: Oxidation of Metals, Journal Name: Oxidation of Metals Journal Issue: 3-4 Vol. 47; ISSN OXMEAF; ISSN 0030-770X
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ADHESION
ALUMINIUM ALLOYS
CHROMIUM ALLOYS
CORROSION RESISTANCE
NICKEL BASE ALLOYS
SCALING
TEMPERATURE RANGE 0400-1000 K
TEMPERATURE RANGE 1000-4000 K
THERMAL CYCLING