Excimer laser induced photolytic deposition of aluminum nitride: Film growth and properties
- Aerospace Corp., Los Angeles, CA (United States). Mechanics and Materials Technology Center
Excimer laser photolysis has been used for the growth of smooth and well-adhering thin films of aluminum nitride (AlN) on Si, fused quartz, and KBr substrates at temperatures as low as 350 K. The photolysis was carried out at 193 nm, with the laser beam propagating parallel to the substrate. Trimethylamine alane and ammonia were used as gas-phase precursors. The growth rate of these films was investigated as a function of laser fluence. These measurements, as well as other investigations of film growth with and without the photolysis laser, reveal that no AlN film is produced in the absence of laser-induced photolysis of the precursors. The morphology and physical properties of these laser-grown films have been studied by scanning electron microscopy, X-ray diffraction, and transmission electron microscopy. Optical absorption spectra of films grown on fused quartz were measured as a function of substrate temperature. A substrate temperature of 350 K was found to be optimum for obtaining good film quality while precluding any effects due to the thermal decomposition of the precursors. The films have excellent dielectric properties as shown by I-V and C-V measurements. The details of AlN film growth using low-temperature gas-phase photolysis at 193 nm and the characterization of these laser grown films will be discussed.
- OSTI ID:
- 490901
- Report Number(s):
- CONF-951155--; ISBN 1-55899-300-2
- Country of Publication:
- United States
- Language:
- English
Similar Records
Excimer laser-controlled photochemical deposition of thin films and artificially structured materials
AlN grown by metalorganic molecular beam epitaxy