ELECTRICAL RESISTIVITY OF RARE-EARTH ALLOYS
Technical Report
·
OSTI ID:4717538
Resistivities of solid solution alloys in the systems Gd-Lu, Tb-- Lu, Gd- - Er, and Y-Lu were measured at 4.2 to 320 deg K to determine the behavior of the resistivity in alloy systems with magnetic phenomena arising from localized magnetic moments, A large contribution to the residual resistivity is caused by the random distribution of these localized moments through the lattice. An analysis of the lattice resistivity of the metals shows large variations across the heavy rare-earth series which are possibly correlated with the change of c/a ratio of the metals and the attendent changes in the Fermi surface geometry. (auth)
- Research Organization:
- Ames Lab., Ames, Iowa
- DOE Contract Number:
- W-7405-ENG-82
- NSA Number:
- NSA-17-011190
- OSTI ID:
- 4717538
- Report Number(s):
- IS-477
- Country of Publication:
- United States
- Language:
- English
Similar Records
MECHANISMS OF THE ELECTRICAL RESISTIVITY OF RARE EARTH ALLOYS AT LOW TEMPERATURES
Electrical Resistivity of Dilute Alloys of Rare Earths with Yttrium at Low Temperatures
Magnetic and hysteresis properties of compounds of rare earth metals with iron
Thesis/Dissertation
·
Sun Dec 31 23:00:00 EST 1961
·
OSTI ID:4769475
Electrical Resistivity of Dilute Alloys of Rare Earths with Yttrium at Low Temperatures
Journal Article
·
Mon Jul 15 00:00:00 EDT 1963
· Journal of the Physical Society of Japan
·
OSTI ID:4648797
Magnetic and hysteresis properties of compounds of rare earth metals with iron
Journal Article
·
Wed Oct 31 23:00:00 EST 1973
· Fiz. Metal. Metalloved., v. 36, no. 5, pp. 965-970
·
OSTI ID:4336619