CORROSION OF EXPERIMENTAL ALUMINUM ALLOYS IN HIGH TEMPERATURE WATER. Report No. 8
Technical Report
·
OSTI ID:4349725
The alloys tested in high-temperature water include X-2219 (Al--6 wt.% Cu), M-388(A1--1 wt.% Ni--0.5 wt.% Fe), and M-400 (Al--1 wt.% Ni--1 wt.% Fe). Static autoclave tests were made at 680 deg F in both saturated steam and water and at 600 deg F in water. Circulating autoclave tests were made at 680 deg F in water at pH values of 3.5, 4.0, 4.5, and 5.0. (J.E.D.)
- Research Organization:
- Westinghouse Electric Corp. Bettis Plant, Pittsburgh
- NSA Number:
- NSA-12-001372
- OSTI ID:
- 4349725
- Report Number(s):
- WAPD-PWR-PMM-1062
- Country of Publication:
- United States
- Language:
- English
Similar Records
CORROSION OF EXPERIMENTAL ALUMINUM ALLOYS IN HIGH TEMPERATURE WATER. Report No. 9
CORROSION OF EXPERIMENTAL ALUMINUM ALLOYS IN HIGH TEMPERATURE WATER. Report No. 7
SUMMARY OF CORROSION INVESTIGATIONS ON HIGH-TEMPERATURE ALUMINUM ALLOYS. Period covered : February 1955-October 1956
Technical Report
·
Thu Aug 22 00:00:00 EDT 1957
·
OSTI ID:4330634
CORROSION OF EXPERIMENTAL ALUMINUM ALLOYS IN HIGH TEMPERATURE WATER. Report No. 7
Technical Report
·
Thu Dec 20 23:00:00 EST 1956
·
OSTI ID:4299589
SUMMARY OF CORROSION INVESTIGATIONS ON HIGH-TEMPERATURE ALUMINUM ALLOYS. Period covered : February 1955-October 1956
Technical Report
·
Sun Jan 31 23:00:00 EST 1960
·
OSTI ID:4204344