CORROSION OF EXPERIMENTAL ALUMINUM ALLOYS IN HIGH TEMPERATURE WATER. Report No. 7
Technical Report
·
OSTI ID:4299589
Corrosion data for tests of Al--Fe--Ni alloy in 680 deg F H/sub 2/O-- steam, 600 deg F static H/sub 2/O, 580 deg F circulating H/sub 2/O at pH 6.5 to 7.5, and 680 deg F circulating H/sub 2/O at pH 3.5 and 4 with H/sub 3/PO/sub 4/ are tabulated and discussed. Results from 650 deg F dynamic water tests at 20 fps and pH 8.5to 9.0 with NH/sub 4/OH 3.5 with H/sub 3/PO/sub 4/ are included. The data were calculatcd from resulis obtained by the iodine --methyl alcohol dissolution method. (T.R.H.)
- Research Organization:
- Westinghouse Electric Corp. Bettis Plant, Pittsburgh
- NSA Number:
- NSA-12-016363
- OSTI ID:
- 4299589
- Report Number(s):
- WAPD-PWR-PMM-1025
- Country of Publication:
- United States
- Language:
- English
Similar Records
CORROSION OF EXPERIMENTAL ALUMINUM ALLOYS IN HIGH TEMPERATURE WATER. Report No. 9
CORROSION OF EXPERIMENTAL ALUMINUM ALLOYS IN HIGH TEMPERATURE WATER. Report No. 8
ZIRCALOY-4 CORROSION IN HALIDE SOLUTIONS AND AT CREVICES IN HIGH- TEMPERATURE WATER
Technical Report
·
Thu Aug 22 00:00:00 EDT 1957
·
OSTI ID:4330634
CORROSION OF EXPERIMENTAL ALUMINUM ALLOYS IN HIGH TEMPERATURE WATER. Report No. 8
Technical Report
·
Sun Mar 31 23:00:00 EST 1957
·
OSTI ID:4349725
ZIRCALOY-4 CORROSION IN HALIDE SOLUTIONS AND AT CREVICES IN HIGH- TEMPERATURE WATER
Technical Report
·
Sun Mar 18 23:00:00 EST 1962
·
OSTI ID:4792968