CORROSION OF EXPERIMENTAL ALUMINUM ALLOYS IN HIGH TEMPERATURE WATER. Report No. 9

Technical Report · Thu Aug 22 04:00:00 EDT 1957

OSTI ID:4330634

Cohen, I

The alloys tested lncluded x-2219 (Al--6 wt.% Cu), M-388 (Al--1 wt.% Ni-- 0.5 wt.% Fe), M-400 (Al--1 wt. % Ni--1 wt.% Fe), 192263 (Al--1.38 wt.% Ni--1.44 wt.% Fe), 1992264 (Al--2.64 wt.% Ni--0.35 wt.% Fe--0.35 wt.% Cr), and 192265 (Al-- 4.34 wt.% Ni--0.76 wt.% Cu--0.38 wt.% Fe). Static autoclave tests were made at 680 deg F in both saturated steam and water and at 600 deg F in water. Circulating autoclave tests were made at 680 deg F in neutral water with and without SbO/sup 3/ addition. Dynamic loop corrosion tests were run at 600 deg F in pH 8.5 to 9.4 water. Dynamic loop corrosion tests were run at 650 deg F in pH 7.0 water with 30 cc/kg of H/sub 2/. (J.E.D.)

• Research Organization: Westinghouse Electric Corp. Bettis Plant, Pittsburgh
• NSA Number: NSA-12-001373
• OSTI ID: 4330634
• Report Number(s): WAPD-PWR-PMM-1247
• Country of Publication: United States
• Language: English

Related Subjects

ACIDITY
ALUMINUM ALLOYS
ANTIMONY OXIDES
CHROMIUM ALLOYS
COPPER ALLOYS
CORROSION
HYDROGEN
IRON ALLOYS
MATERIALS TESTING
MINERALOGY, METALLURGY, AND CERAMICS
NICKEL ALLOYS
PIPES
PRESSURE VESSELS
WATER