PRELIMINARY REPORT ON THE METAL POWDER SLIP CASTING PROCESS. PART II
Technical Report
·
OSTI ID:4303496
The first part of this report concerns the various possibilities for movement of a powder particle in a liquid and shows that on account of this movement an improved particle packing system is achieved. The second part deals with the pH factor of the slip and the effect of this variable on the density of compacts, ascast, dried, and as-sintered. The conclusion is drawn that the pH factor affects the density of the specimen in various stages of the process but probably does not contribute to the sinterability of the slip-cast compact. The third part concerns the strength and elongation of slip cast and sintered 316 stainless steel, and it is attempted to explain tbe high value for elongation with the grain structure of the material. (auth)
- Research Organization:
- Hausner (Henry H.), New York
- NSA Number:
- NSA-12-011451
- OSTI ID:
- 4303496
- Report Number(s):
- NYO-8664
- Country of Publication:
- United States
- Language:
- English
Similar Records
SLIP CASTING OF METAL POWDERS. PART III. Final Report
PRELIMINARY REPORT ON THE METAL POWDER SLIP CASTING PROCESS. PART I
THE FORMING OF COMPLICATED SHAPES BY POWDER METALLURGY SLIP CASTING
Technical Report
·
Wed Feb 11 23:00:00 EST 1959
·
OSTI ID:4267755
PRELIMINARY REPORT ON THE METAL POWDER SLIP CASTING PROCESS. PART I
Technical Report
·
Sun Sep 01 00:00:00 EDT 1957
·
OSTI ID:4330808
THE FORMING OF COMPLICATED SHAPES BY POWDER METALLURGY SLIP CASTING
Technical Report
·
Fri Aug 15 00:00:00 EDT 1958
·
OSTI ID:4323660