DEGRADATION OF PLASTICIZED P.V.C. COMPOSITIONS UNDER HIGH-LEVEL GAMMA RADIATION
Journal Article
·
· Nuclear Power
OSTI ID:4295440
A series of tests was carried out on plasticized polyvinyl chloride samples to determine quantitatively the effect of formulation in preventing or retarding degradation. The results indicate that polyvinyl chloride compounds plasticized with tritolyl phosphate show less physical deterioration under gamma radiation than the other plasticizers tested. (W.D.M.)
- Research Organization:
- Atomic Energy Research Establishment, Harwell, Berks, Eng.
- NSA Number:
- NSA-13-005106
- OSTI ID:
- 4295440
- Journal Information:
- Nuclear Power, Journal Name: Nuclear Power Vol. 4; ISSN 0546-8981; ISSN NUPOAS
- Country of Publication:
- United Kingdom
- Language:
- English
Similar Records
THE DEGRADATION OF PLASTICISED P.V.C. COMPOSITIONS UNDER HIGH LEVEL GAMMA RADIATION. Interim Report
THE DEGRADATION OF PLASTICISED PVC COMPOSITIONS UNDER HIGH LEVEL GAMMA RADIATION. PART 2
EFFECTS OF PLASTICIZERS ON RESISTANCE OF POLYVINYL CHLORIDE TO GAMMA IRRADIATION
Technical Report
·
Thu May 01 00:00:00 EDT 1958
·
OSTI ID:4312658
THE DEGRADATION OF PLASTICISED PVC COMPOSITIONS UNDER HIGH LEVEL GAMMA RADIATION. PART 2
Technical Report
·
Mon May 01 00:00:00 EDT 1961
·
OSTI ID:4018961
EFFECTS OF PLASTICIZERS ON RESISTANCE OF POLYVINYL CHLORIDE TO GAMMA IRRADIATION
Technical Report
·
Tue Dec 31 23:00:00 EST 1957
·
OSTI ID:4730511