CONDITIONS OF /cap beta/ PHASE STABILIZATION IN Ti-Mo-Mn ALLOYS (in Russian)
Journal Article
·
· Zhur. Neorg. Khim.
OSTI ID:4221178
The phase diagrams of magnesium thermal Ti- Mo- Mn alloys are plotted at 700 to 1000 deg C. The beta phase stability at 100 to 600 deg C was studied. In alloys with 17.87% Mn and 1.56% Mo the beta phase is stable during soaking for about 100 hours at 100 to 500 deg C, while in the other alloy's the beta phase disintegrates into beta + omega yields beta + alpha during which the concentrations of Mo and Mn increase and the parameter of the beta phase lattice diminishes. (R.V.J.)
- Research Organization:
- Originating Research Org. not identified
- NSA Number:
- NSA-14-004578
- OSTI ID:
- 4221178
- Journal Information:
- Zhur. Neorg. Khim., Journal Name: Zhur. Neorg. Khim. Vol. Vol: 4
- Country of Publication:
- Country unknown/Code not available
- Language:
- Russian
Similar Records
STABILITY OF THE /cap beta/ PHASE IN Ti-Fe AND Ti-Ni ALLOYS
THE EFFECT OF ALUMINUM ON THE STABILITY OF THE BETA PHASE IN Ti-Mo-Fe ALLOYS
Structure and properties of the annealed alloys of the Ti--Mo system
Journal Article
·
Fri May 01 00:00:00 EDT 1959
· Zhur. Neorg. Khim.
·
OSTI ID:4215969
THE EFFECT OF ALUMINUM ON THE STABILITY OF THE BETA PHASE IN Ti-Mo-Fe ALLOYS
Journal Article
·
Tue Sep 11 00:00:00 EDT 1962
· Doklady Akad. Nauk SSSR
·
OSTI ID:4772581
Structure and properties of the annealed alloys of the Ti--Mo system
Journal Article
·
Sun Dec 31 23:00:00 EST 1972
· Izv. Vyssh. Ucheb. Zaved., Tsvet. Met., no. 3, pp. 120-124
·
OSTI ID:4404797