Stacking faults in austempered ductile iron
- CNEA, San Martin (Argentina). Dept. de Materiales
During last decade, Austempered Ductile Iron (ADI) has been successfully used as an acceptable replacement material for steel in many applications, due to the relatively high strength and reasonable ductility obtained. These properties are the result of the special microstructure exhibited by this material at the end of the upper bainite reaction: ferrite platelets surrounded by high carbon stabilized austenite. However, at the beginning of the austempering treatment, the existence of interdendritic low carbon austenite is revealed by its transformation to martensite when cooling the sample or during subsequent deformation. The completion of the upper bainite reaction is of decisive importance to mechanical properties because the remaining martensite reduces ductility. It was observed that the rate of the upper bainite reaction is governed by the carbon content difference between the low and high carbon austenites. The carbon content is obtained by the lattice parameter measurement, because there exists a known expression that relates both magnitudes. Several works have used X-ray diffraction to measure the lattice parameter and phase concentrations as a function of austempering time. In these works, the lattice parameters were obtained directly from the {l_brace}220{r_brace} and {l_brace}311{r_brace} peaks position. The purpose of this work is to show more precise lattice parameters measurement and, very closely related to this, the existence of stacking faults in austenite, even at times within the processing window.
- OSTI ID:
- 250700
- Journal Information:
- Scripta Materialia, Journal Name: Scripta Materialia Journal Issue: 11 Vol. 34; ISSN 1359-6462; ISSN XZ503X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Influence of microstructure on fracture toughness of austempered ductile iron
Effect of austempering time on mechanical properties of a low manganese austempered ductile iron