Effect of austempering time on mechanical properties of a low manganese austempered ductile iron
An investigation was carried out to examine the influence of austempering time on the resultant microstructure and the room-temperature mechanical properties of an unalloyed and low manganese ductile cast iron with initially ferritic as-cast structure. The effect of austempering time on the plane strain fracture toughness of this material was also studied. Compact tension and round cylindrical tensile specimens were prepared from unalloyed ductile cast iron with low manganese content and with a ferritic as-cast (solidified) structure. These specimens were then austempered in the upper (371 C) and lower (260 C) bainitic temperature ranges for different time periods, ranging from 30 min. to 3 h. Microstructural features such as type of bainite and the volume fraction of ferrite and austenite and its carbon content were evaluated by X-ray diffraction to examine the influence of microstructure on the mechanical properties and fracture toughness of this material. The results of the present investigation indicate that for this low manganese austempered ductile iron (ADI), upper ausferritic microstructures exhibit higher fracture toughness than lower ausferritic microstructures. Yield and tensile strength of the material was found to increase with an increase in austempering time in a lower bainitic temperature range, whereas in the upper bainitic temperature range, time has no significant effect on the mechanical properties. A retained austenite content between 30 to 35% was found to provide optimum fracture toughness. Fracture toughness was found to increase with the parameter (X{gamma}C{gamma}/d){sup 1/2}, where X{gamma} is the volume fraction of austenite, C{gamma} is the carbon content of the austenite, and d is the mean free path of dislocation motion in ferrite.
- Research Organization:
- Wayne State Univ., Detroit, MI (US)
- OSTI ID:
- 20075693
- Journal Information:
- Journal of Materials Engineering and Performance, Journal Name: Journal of Materials Engineering and Performance Journal Issue: 2 Vol. 9; ISSN 1059-9495; ISSN JMEPEG
- Country of Publication:
- United States
- Language:
- English
Similar Records
Influence of microstructure on fracture toughness of austempered ductile iron
Electron microstructure and mechanical properties of silicon and aluminum ductile irons