Glass transition and composite formation in InF{sub 3}-containing oxyfluoroniobate system
- Institute of Chemistry FEB RAS, Vladivostok (Russian Federation)
- All-Russian Scientific Research Institute of Aviation Materials (Russian Federation)
The glasses in the system MnNbOF{sub 5}-BaF{sub 2}-InF{sub 3} have been firstly synthesized and studied. The thermal parameters of these glasses are analyzed. It was stated that glass of the composition 40MnNbOF{sub 5}-40BaF{sub 2}-20InF{sub 3} is the most thermal stable in the system under study. By X-ray analysis the compositions of the crystalline phases obtained at the glass thermal treatment were determined: the main phases are Ba{sub 3}In{sub 2}F{sub 12} and BaNbOF{sub 5}. By Raman and IR spectra analysis it was stated that the networks of glasses in the system are built by the structural type of the glasses in NbO{sub 2}F-BaF{sub 2} system: (NbO{sub n}F{sub m}) polyhedra joined oxygen bridges. Indium trifluoride forms InF{sub 6} polyhedra, which are embeded between oxyfluoroniobate ions, forming a common networks or forms its own layers from InF{sub 6} polyhedra. IR-spectroscopy method showed that at devitrification of the sample 30MnNbOF{sub 5}-50BaF{sub 2}-20InF{sub 3} the band position and shape change in going from glass state to crystalline. The bands in the range 900–700 cm{sup −1} shift into the low-frequency range and transformed into narrow peaks characteristic for the crystalline state. It was determined that for this sample the IR-spectroscopy method fixes the presence of the crystalline phases at 340°C without time of exposure, despite the fact that X-ray analysis shows an amorphous state for this sample at the same temperature. It was suggested, that controlling the composition and conditions of annealing of the glasses it can be obtain the transparent glass-ceramics of definite composition.
- OSTI ID:
- 22609171
- Journal Information:
- AIP Conference Proceedings, Vol. 1736, Issue 1; Conference: 8. international conference on times of polymers and composites: From aerospace to nanotechnology, Naples (Italy), 19-23 Jun 2016; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structure and properties of certain glasses based on the PbO-B/sub 2/O/sub 3/ system
Luminescence of phosphorus containing oxide materials: Crystalline SiO{sub 2}‐P and 3P{sub 2}O{sub 5}⋅7SiO{sub 2}; CaO⋅P{sub 2}O{sub 5}; SrO⋅P{sub 2}O{sub 5} glasses