Luminescence of phosphorus containing oxide materials: Crystalline SiO{sub 2}‐P and 3P{sub 2}O{sub 5}⋅7SiO{sub 2}; CaO⋅P{sub 2}O{sub 5}; SrO⋅P{sub 2}O{sub 5} glasses
- impactGlass research international, 3938 E Grant Rd #131, Tucson, AZ 85712 (United States)
Luminescence of phosphate glasses such as CaO⋅P{sub 2}O{sub 5} and SrO⋅P{sub 2}O{sub 5} is compared with that of phosphorus doped crystalline α-quartz and phosphosilicate glass with content 3P{sub 2}O{sub 5}⋅7SiO{sub 2}. Water and OH groups are found by IR spectra in these materials. The spectrum of luminescence contains many bands in the range 1.5 - 5.5 eV. The luminescence bands in UV range at 4.5-5 eV are similar in those materials. Decay duration in exponential approximation manifests a time constant about 37 ns. Also a component in μs range was detected. PL band of μs component is shifted to low energy with respect to that of ∼37 ns component. This shift is about 0.6 eV. It is explained as singlet-triplet splitting of excited state. Below 14 K increase of luminescence kinetics duration in μs range was observed and it was ascribed to zero magnetic field splitting of triplet excited state of the center. Yellow-red luminescence was induced by irradiation in phosphorus doped crystalline α-quartz, phosphosilicate glasses. The yellowl uminescence contains two bands at 600 and 740 nm. Their decay is similar under 193 nm laser and may be fitted with the first order fractal kinetics or stretched exponent. Thermally stimulated luminescence contains only band at 600 nm. The 248 nm laser excites luminescence at 740 nm according to intra center process with decay time constant about 4 ms at 9 K. Both type of luminescence UV and yellow were ascribed to different defects containing phosphorus. P-doped α-quartz sample heated to 550 co become opalescent. Ir spectra related to water and OH groups are changed. Photoluminescence intensity of all three bands, UV (250 nm), yellow (600 nm) and red (740 nm) strongly diminished and disappeared after heating to 660 C°. Radiation induced red luminescence of non-bridging oxygen luminescence center (NBO) appeared in crystal after heat treatment. We had observed a crystalline version of this center (l. Skuja et al, Nuclear Instruments and Methods in Physics Research B 286,159-168 (2012)). Effect of heat treatment explained as sedimentation of phosphorus in some state. Keeping of treated sample at 450-500 C° leads to partial revival of ability to create yellow luminescence center under irradiation.
- OSTI ID:
- 22308114
- Journal Information:
- AIP Conference Proceedings, Vol. 1624, Issue 1; Conference: SIO2014: 10. international symposium on SiO2, advanced dielectrics and related devices, Cagliari (Italy), 16-18 Jun 2014; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Study of carrier recombination transient characteristics in MOCVD grown GaN dependent on layer thickness
White light generation from Dy{sup 3+}-doped ZnO-B{sub 2}O{sub 3}-P{sub 2}O{sub 5} glasses
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
COMPARATIVE EVALUATIONS
CRYSTALS
DOPED MATERIALS
EV RANGE
EXCITED STATES
FRACTALS
HEAT TREATMENTS
INFRARED SPECTRA
IRRADIATION
MAGNETIC FIELDS
PHOSPHATE GLASS
PHOTOLUMINESCENCE
QUARTZ
SILICON OXIDES
TEMPERATURE DEPENDENCE
THERMOLUMINESCENCE
TRIPLETS