The influences of mole composition of strontium (x) on properties of barium strontium titanate (Ba{sub 1−x}Sr{sub x}TiO{sub 3}) prepared by solid state reaction method

Journal Article · Mon Feb 08 04:00:00 EST 2016 · AIP Conference Proceedings

DOI:https://doi.org/10.1063/1.4941472· OSTI ID:22494605

Sandi, Dianisa Khoirum; Supriyanto, Agus; Iriani, Yofentina ^[1]; Jamaluddin, Anif ^[2]

---

1. Physics Department, Faculty of Mathematics and Natural Science, Sebelas Maret University (Indonesia)
2. Physics Department, Faculty of Teacher Training and Education, Sebelas Maret University (Indonesia)

Barium Strontium Titanate (Ba{sub 1-x}Sr{sub x}TiO{sub 3}) or BST was prepared by solid state reaction method. Raw materials are BaCO{sub 3}, SrCO{sub 3}, and TiO{sub 2}. Those materials are mixed for 8 h, pressed, and sintered at temperature 1200°C for 2 h. Mole composition of Sr (x) was varied to study its influences on structural, morphological, and electrical properties of BST. Variation of (x) are x = 0; x = 0.1; and x = 0.5. XRD patterns showed a single phase of BST, which mean that mixture of raw materials was homogenous. Crystal structure was influenced by x. BaTiO{sub 3} and Ba{sub 0.9}Ti{sub 0.1}TiO{sub 3} have tetragonal crystal structure, while Ba{sub 0.5}Sr{sub 0.5}TiO{sub 3} is cubic. The diffraction angle shifted to right side (angle larger) as the increases of x. Crystalline size of BaTiO{sub 3}, Ba{sub 0.9}Sr{sub 0.1}TiO{sub 3}, and Ba{sub 0.5}Sr{sub 0.5}TiO{sub 3} are 38.13 nm; 38.62 nm; and 37.13 nm, respectively. SEM images showed that there are still of pores which were influenced by x. Ba{sub 0.9}Sr{sub 0.1}TiO{sub 3} has densest surface (pores are few and small in size). Sawyer Tower circuit showed that BaTiO{sub 3} and Ba{sub 0.9}Sr{sub 0.1} TiO{sub 3} is ferroelectric, while Ba{sub 0.5}Sr{sub 0.5}TiO{sub 3} is paraelectric. The dielectric constants of BaTiO{sub 3}, Ba{sub 0.9}Sr{sub 0.1}TiO{sub 3} and Ba{sub 0.5}Sr{sub 0.5}TiO{sub 3} at frequency of 1 KHz are 156; 196; and 83, respectively. Ba{sub 0.9}Sr{sub 0.1}TiO{sub 3} has relatively highest dielectric constant. It is considered that Ba{sub 0.9}Sr{sub 0.1}TiO{sub 3} has densest surface.

• OSTI ID: 22494605
• Journal Information: AIP Conference Proceedings, Journal Name: AIP Conference Proceedings Journal Issue: 1 Vol. 1710; ISSN APCPCS; ISSN 0094-243X
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
71 CLASSICAL AND QUANTUM MECHANICS
GENERAL PHYSICS
BARIUM
BARIUM CARBONATES
COOLING TOWERS
CRYSTAL STRUCTURE
FERROELECTRIC MATERIALS
IMAGES
KHZ RANGE 01-100
MIXTURES
PERMITTIVITY
POWER TRANSMISSION TOWERS
PRESSES
RAW MATERIALS
SCANNING ELECTRON MICROSCOPY
SOLIDS
STRONTIUM
STRONTIUM CARBONATES
SURFACES
TITANATES
TITANIUM OXIDES
VARIATIONS
X-RAY DIFFRACTION