Structural and magnetic properties of pure and Cu doped In{sub 2}O{sub 3} thin films
Journal Article
·
· AIP Conference Proceedings
- Thin Films Laboratory, School of Advanced Sciences, VIT University, Vellore – 632014 (India)
- Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam –603102 (India)
Pure and Cu (7 at.%) doped In{sub 2}O{sub 3} thin films were prepared using an electron beam evaporation technique. A systematic study was carried out on the structural, chemical and magnetic properties of the thin films. X-ray diffraction analysis revealed that all the films were cubic in structure. The pure and Cu doped In{sub 2}O{sub 3} thin films showed ferromagnetism at room temperature. The Cu doped In{sub 2}O{sub 3} thin films showed the saturation magnetization, coercivity and retentivity of 38.71 emu/cm{sup 3}, 245 G and 5.54 emu/cm{sup 3}, respectively.
- OSTI ID:
- 22490559
- Journal Information:
- AIP Conference Proceedings, Journal Name: AIP Conference Proceedings Journal Issue: 1 Vol. 1665; ISSN APCPCS; ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structure and magnetic properties of Fe doped In{sub 2}O{sub 3} thin films prepared by electron beam evaporation
Room temperature ferromagnetism in undoped and Ni doped In{sub 2}O{sub 3} thin films
Room Temperature Ferromagnetism in Cu Doped ZnO Thin Films
Journal Article
·
Wed Jun 24 00:00:00 EDT 2015
· AIP Conference Proceedings
·
OSTI ID:22490565
Room temperature ferromagnetism in undoped and Ni doped In{sub 2}O{sub 3} thin films
Journal Article
·
Wed Jun 24 00:00:00 EDT 2015
· AIP Conference Proceedings
·
OSTI ID:22490561
Room Temperature Ferromagnetism in Cu Doped ZnO Thin Films
Journal Article
·
Fri Jul 15 00:00:00 EDT 2011
· AIP Conference Proceedings
·
OSTI ID:21608129