Fe modified BaTiO{sub 3}: Influence of doping on ferroelectric property

Journal Article · Wed Jun 24 00:00:00 EDT 2015 · AIP Conference Proceedings

DOI:https://doi.org/10.1063/1.4917631· OSTI ID:22490213

Mishra, Ashutosh; Bisen, Supriya; Jarabana, Kanaka Mahalakshmi; Mishra, Niyati ^[1]

---

1. School of Physics, Devi Ahilya University, Khandwa Road, Indore-452001 (India)

We have investigate the ferroelectric property of Fe modified Barium Titanate (BaTiO{sub 3}) with possible tetragonal structure via solid state route was prepared. Modified sample of BaTi{sub 1−x}Fe{sub x}O{sub 3} (x=0.01, 0.02) were structural characterized by X-ray Diffraction (XRD) using a Bruker D8 Advance XRD instruments, the value of 2θ is in between 20° to 80°. Fourier transform infrared spectroscopy (FTIR) using a Bruker, vertex instruments has been performs to obtain Ti-O bonding in the modified sample; the region of wavenumber is from 4000 cm{sup −1} to 400 cm{sup −1}. P-E hysteresis loop measurements have been traced for different applied voltage- 100V, 300V and 500V.

• OSTI ID: 22490213
• Journal Information: AIP Conference Proceedings, Journal Name: AIP Conference Proceedings Journal Issue: 1 Vol. 1665; ISSN APCPCS; ISSN 0094-243X
• Country of Publication: United States
• Language: English

Related Subjects

75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ABSORPTION SPECTROSCOPY
BARIUM COMPOUNDS
CHEMICAL BONDS
CONCENTRATION RATIO
ELECTRIC POTENTIAL
FERROELECTRIC MATERIALS
FOURIER TRANSFORMATION
HYSTERESIS
INFRARED SPECTRA
IRON COMPOUNDS
SOLIDS
TETRAGONAL LATTICES
TITANATES
X-RAY DIFFRACTION