Structural analysis and ferroelectric properties of Fe doped BaTiO{sub 3}
- School of Physics, Devi Ahilya University, Khandwa road campus, Indore, 452001 (India)
The polycrystalline samples of Fe doped BaTiO{sub 3} (BTO) with compositional formula BaTi{sub 1-x}Fe{sub x}O{sub 3} (x = 0, 0.03, 0.04 and 0.05) were prepared by solid-state reaction route. The influence of the Fe content on the structural, vibrational and electric properties of BaTiO{sub 3} was investigated using X-ray powder diffraction (XRD), Raman spectroscopy and Polarization techniques. XRD analysis indicates the formation of single-phase tetragonal structure for all the prepared samples. Tetragonal cubic structure with space group P4mm of all samples is further approved by Rietveld refinement. Room temperature Raman spectra of pure BaTiO{sub 3} show four active modes of vibration whose intensity decreases with increasing Fe doping. Small shift in Raman modes and increment in the line width has been observed with the doping ions. The hysteresis loop is very well performed with regular sharp characteristic of ferroelectric materials.
- OSTI ID:
- 22608736
- Journal Information:
- AIP Conference Proceedings, Journal Name: AIP Conference Proceedings Journal Issue: 1 Vol. 1731; ISSN APCPCS; ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Fe modified BaTiO{sub 3}: Influence of doping on ferroelectric property
Ferroelectric, and piezoelectric properties of BaTi{sub 1−x}Al{sub x}O{sub 3}, 0 ≤ x ≤ 0.015
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
BARIUM COMPOUNDS
DOPED MATERIALS
ELECTRICAL PROPERTIES
FERROELECTRIC MATERIALS
HYSTERESIS
IRON ADDITIONS
LINE WIDTHS
POLARIZATION
POLYCRYSTALS
POWDERS
RAMAN SPECTRA
RAMAN SPECTROSCOPY
SOLIDS
SPACE GROUPS
TEMPERATURE RANGE 0273-0400 K
TETRAGONAL LATTICES
TITANATES
X-RAY DIFFRACTION