Phase equilibria in the quasiternary system Ag{sub 2}S–Ga{sub 2}S{sub 3}–In{sub 2}S{sub 3} and optical properties of (Ga{sub 55}In{sub 45}){sub 2}S{sub 300}, (Ga{sub 54.59}In{sub 44.66}Er{sub 0.75}){sub 2}S{sub 300} single crystals

Journal Article · Wed Jul 15 04:00:00 EDT 2015 · Journal of Solid State Chemistry

DOI:https://doi.org/10.1016/J.JSSC.2015.04.006· OSTI ID:22475705

Danyliuk, I. V. ^[1]; Olekseyuk, I. D.; Pankevych, V. Z. ^[2]; Halyan, V. V. ^[3]

---

1. Department of Ecology and Environmental Protection, Eastern European National University, Lutsk (Ukraine)
2. Department of Inorganic and Physical Chemistry, Eastern European National University, Lutsk (Ukraine)
3. Department of General Physics, Eastern European National University, Lutsk (Ukraine)

The quasiternary system Ag{sub 2}S–Ga{sub 2}S{sub 3}–In{sub 2}S{sub 3} was investigated by differential thermal, X-ray diffraction analyses. The phase diagram of the Ga{sub 2}S{sub 3}–In{sub 2}S{sub 3} system and nine polythermal sections, isothermal section at 820 K and the liquidus surface projection were constructed. The existence of the large solid solutions ranges of binary and ternary compounds was established. The range of the existence of the quaternary phase AgGa{sub x}In{sub 5−x}S{sub 8} (2.25≤x≤2.85) at 820 K was determined. The single crystals (Ga{sub 55}In{sub 45}){sub 2}S{sub 300} and (Ga{sub 54.59}In{sub 44.66}Er{sub 0.75}){sub 2}S{sub 300} were grown by a directional crystallization method from solution-melt. Optical absorption spectra in the 500–1600 nm range were recorded. The luminescence of the (Ga{sub 54.59}In{sub 44.66}Er{sub 0.75}){sub 2}S{sub 300} single crystal shows a maximum at 1530 nm for the excitation wavelengths of 532 and 980 nm at 80 and 300 K. - Graphical abstract: Isothermal section of the quasiternary system Ag{sub 2}S–Ga{sub 2}S{sub 3}–In{sub 2}S{sub 3} at 820 K and normalized photoluminescence spectra of the single crystal (Ga{sub 54.59}In{sub 44.66}Er{sub 0.75}){sub 2}S{sub 300} at 300 K. - Highlights: • Isothermal section at 820 K, liquidus surface projection were built for Ag{sub 2}S–Ga{sub 2}S{sub 3}–In{sub 2}S{sub 3}. • Optical properties of single crystals were studied.

• OSTI ID: 22475705
• Journal Information: Journal of Solid State Chemistry, Journal Name: Journal of Solid State Chemistry Vol. 227; ISSN 0022-4596; ISSN JSSCBI
• Country of Publication: United States
• Language: English

Related Subjects

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CHEMISTRY
ABSORPTION SPECTRA
CRYSTALLIZATION
EMISSION SPECTRA
ERBIUM SULFIDES
EXCITATION
GALLIUM SULFIDES
INDIUM SULFIDES
MONOCRYSTALS
OPTICAL PROPERTIES
PHASE DIAGRAMS
PHOTOLUMINESCENCE
SILVER SULFIDES
SOLID SOLUTIONS
SURFACES
TEMPERATURE DEPENDENCE
X-RAY DIFFRACTION