Phase equilibria in the quasi-ternary system Ag{sub 2}Se–Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} and physical properties of (Ga{sub 0.6}In{sub 0.4}){sub 2}Se{sub 3}, (Ga{sub 0.594}In{sub 0.396}Er{sub 0.01}){sub 2}Se{sub 3} single crystals

Journal Article · Sat Feb 15 04:00:00 EST 2014 · Journal of Solid State Chemistry

DOI:https://doi.org/10.1016/J.JSSC.2013.11.004· OSTI ID:22274200

Danyliuk, I. V.; Olekseyuk, I. D. ^[1]; Halyan, V. V. ^[2]

---

1. Department of Inorganic and Physical Chemistry, Eastern European National University, Voli Ave 13, Lutsk 43025 (Ukraine)
2. Department of General Physics, Eastern European National University, Voli Ave 13, Lutsk 43025 (Ukraine)

The quasi-ternary system Ag{sub 2}Se–Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} was investigated by differential thermal, X-ray phase, X-ray structure, microstructure analysis and microhardness measurements. Five quasi-binary phase diagrams, six polythermal sections, isothermal section at 820 K and the liquidus surface projection were constructed. The character and temperature of the invariant processes were determined. The specific resistance of the single crystals (Ga{sub 0.6}In{sub 0.4}){sub 2}Se{sub 3}, (Ga{sub 0.594}In{sub 0.396}Er{sub 0.01}){sub 2}Se{sub 3} was measured, 7.5×10{sup 5} and 3.15×10{sup 5} Ω m, respectively, optical absorption spectra in the 600–1050 nm range were recorded at room temperature, and the band gap energy was estimated which is 1.95±0. 01 eV for both samples. - Graphical abstract: The article reports for the first time the investigated liquidus surface projection of the Ag{sub 2}Se–Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} system and isothermal section at 820 K of the system. Five phase diagrams, six polythermal sections, isothermal section at 820 K and the liquidus surface projection were built at the first time. The existence of the large region of the solid solutions based on AgIn{sub 5}Se{sub 8}, Ga{sub 2}Se{sub 3} and AgGa{sub 1−x}In{sub x}Se{sub 2} was investigated. The existence of two ternary phases was established in the Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} system. Two single crystals (Ga{sub 0.6}In{sub 0.4}){sub 2}Se{sub 3}, (Ga{sub 0.594}In{sub 0.396}Er{sub 0.01}){sub 2}Se{sub 3} were grown and some of optical properties of them were studied at first time. Display Omitted - Highlights: • Liquidus surface projection was built for Ag{sub 2}Se–Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} system. • Solid solution ranges of AgIn{sub 5}Se{sub 8}, Ga{sub 2}Se{sub 3} and AgGa{sub 1−x}In{sub x}Se{sub 2} were investigated. • Two single crystals (Ga{sub 0.6}In{sub 0.4}){sub 2}Se{sub 3}, (Ga{sub 0.594}In{sub 0.396}Er{sub 0.01}){sub 2}Se{sub 3} were grown. • Some optical properties of these single crystals were studied.

• OSTI ID: 22274200
• Journal Information: Journal of Solid State Chemistry, Journal Name: Journal of Solid State Chemistry Journal Issue: 1 Vol. 210; ISSN 0022-4596; ISSN JSSCBI
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CHEMISTRY
ABSORPTION SPECTRA
GALLIUM SELENIDES
MICROHARDNESS
MICROSTRUCTURE
MONOCRYSTALS
OPTICAL PROPERTIES
PHASE DIAGRAMS
SOLID SOLUTIONS
SURFACES
THERMAL ANALYSIS
X RADIATION
X-RAY DIFFRACTION