AlGaN/GaN heterostructure prepared on a Si (110) substrate via pulsed sputtering
- Institute of Industrial Science (IIS), The University of Tokyo, 4-6-1 Komaba, Tokyo 153-8505 (Japan)
GaN films were grown on Si (110) substrates using a low-temperature growth technique based on pulsed sputtering. Reduction of the growth temperature suppressed the strain in the GaN films, leading to an increase in the critical thickness for crack formation. In addition, an AlGaN/GaN heterostructure with a flat heterointerface was prepared using this technique. Furthermore, the existence of a two dimensional electron gas at the heterointerface with a mobility of 1360 cm{sup 2}/Vs and a sheet carrier density of 1.3 × 10{sup 13} cm{sup −2} was confirmed. Finally, the use of the AlGaN/GaN heterostructure in a high electron mobility transistor was demonstrated. These results indicate that low-temperature growth via pulsed sputtering is quite promising for the fabrication of GaN-based electronic devices.
- OSTI ID:
- 22269167
- Journal Information:
- Applied Physics Letters, Vol. 104, Issue 18; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Metalorganic chemical vapor deposition growth of high-mobility AlGaN/AlN/GaN heterostructures on GaN templates and native GaN substrates
High-electron-mobility AlGaN/GaN heterostructures grown on Si(001) by molecular-beam epitaxy