Epitaxial growth of AlN films via plasma-assisted atomic layer epitaxy
- U.S. Naval Research Laboratory, Washington, DC 20375 (United States)
Thin AlN layers were grown at 200–650 °C by plasma assisted atomic layer epitaxy (PA-ALE) simultaneously on Si(111), sapphire (1120), and GaN/sapphire substrates. The AlN growth on Si(111) is self-limited for trimethyaluminum (TMA) pulse of length > 0.04 s, using a 10 s purge. However, the AlN nucleation on GaN/sapphire is non-uniform and has a bimodal island size distribution for TMA pulse of ≤0.03 s. The growth rate (GR) remains almost constant for T{sub g} between 300 and 400 °C indicating ALE mode at those temperatures. The GR is increased by 20% at T{sub g} = 500 °C. Spectroscopic ellipsometry (SE) measurement shows that the ALE AlN layers grown at T{sub g} ≤ 400 °C have no clear band edge related features, however, the theoretically estimated band gap of 6.2 eV was measured for AlN grown at T{sub g} ≥ 500 °C. X-ray diffraction measurements on 37 nm thick AlN films grown at optimized growth conditions (T{sub g} = 500 °C, 10 s purge, 0.06 s TMA pulse) reveal that the ALE AlN on GaN/sapphire is (0002) oriented with rocking curve full width at the half maximum (FWHM) of 670 arc sec. Epitaxial growth of crystalline AlN layers by PA-ALE at low temperatures broadens application of the material in the technologies that require large area conformal growth at low temperatures with thickness control at the atomic scale.
- OSTI ID:
- 22218132
- Journal Information:
- Applied Physics Letters, Journal Name: Applied Physics Letters Journal Issue: 8 Vol. 103; ISSN APPLAB; ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Low temperature epitaxial growth of AlN and GaN thin films by the method of ion beam assisted deposition
Si (111) substrates as highly effective pseudomasks for selective growth of GaN material and devices by ammonia-molecular-beam epitaxy
Control over the morphology of AlN during molecular beam epitaxy with the plasma activation of nitrogen on Si (111) substrates
Book
·
Thu Oct 31 23:00:00 EST 1996
·
OSTI ID:394969
Si (111) substrates as highly effective pseudomasks for selective growth of GaN material and devices by ammonia-molecular-beam epitaxy
Journal Article
·
Mon Apr 24 00:00:00 EDT 2006
· Applied Physics Letters
·
OSTI ID:20779179
Control over the morphology of AlN during molecular beam epitaxy with the plasma activation of nitrogen on Si (111) substrates
Journal Article
·
Sat Feb 14 23:00:00 EST 2015
· Semiconductors
·
OSTI ID:22470063