NiCr etching in a reactive gas
- Institute of Physical High Technology, 9 Albert Einstein Strasse 07745 Jena (Germany)
The authors have etched NiCr through a resist mask using Cl/Ar based chemistry in an electron cyclotron resonance etch system. The optimum gas mixture and etch parameters were found for various ratios of Ni to Cr, based on the etch rate, redeposits, and the etch ratio to the mask. The introduction of O{sub 2} into the chamber, which is often used in the etching of Cr, served to both increase and decrease the etch rate depending explicitly on the etching parameters. Etch rates of >50 nm min{sup -1} and ratios of >1 (NiCr:Mask) were achieved for NiCr (80:20). Pattern transfer from the mask into the NiCr was achieved with a high fidelity and without redeposits for a Cl/Ar mix of 10% Ar (90% Cl{sub 2}) at an etch rate of {approx_equal}50 nm min{sup -1} and a ratio of 0.42 (NiCr:ZEP 7000 e-beam mask)
- OSTI ID:
- 20979366
- Journal Information:
- Journal of Vacuum Science and Technology. A, International Journal Devoted to Vacuum, Surfaces, and Films, Journal Name: Journal of Vacuum Science and Technology. A, International Journal Devoted to Vacuum, Surfaces, and Films Journal Issue: 3 Vol. 25; ISSN 1553-1813
- Country of Publication:
- United States
- Language:
- English
Similar Records
High speed anisotropic reactive ion etching of gold films
High rate reactive ion etch and electron cyclotron resonance etching of GaAs via holes using thick polyimide and photoresist masks