Composites of Upgraded Metallurgical Grade (UMG) Si with Photovoltaic (PV) Grade Si
- Solar Energy Consortium, Kingston, NY (United States); The Solar Energy Consortium
- Solar Energy Consortium, Kingston, NY (United States)
At the beginning of this project 125 wafers of UMG material blended with non-UMG were obtained in the various blends; 50/50,70/30,80/20. 90/10 and 100% UMG. Solar grade, non-UMG material was used for comparison. Many techniques for starting substrate evaluation were used including lifetime, resitivity, SEM, IPCMS. Some degree of gettering was implemented by lengthening the time of phosphorous diffusion. The UMG/solar blends resulted in 14.5% -15% efficiencies, and even 100% UMG showed 14.5% values, not less than standard cells manufactured at the time and an encouraging result for the prospects of using UMG material due to the lower $/watt. A later decline in the cost of Si and an emphasis on reaching higher efficiencies in general led to a vanishing interest in the use of UMG.
- Research Organization:
- Solar Energy Consortium, Kingston, NY (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- EE0000332
- OSTI ID:
- 1176923
- Report Number(s):
- Final 332 TSEC
- Country of Publication:
- United States
- Language:
- English
Similar Records
Characterization of UMG-Based Si Solar Cells
Solar Cell Production using UMG Silicon
Limiting factors for the application of crystalline upgraded metallurgical grade silicon
Conference
·
Mon Sep 06 00:00:00 EDT 2010
·
OSTI ID:1176924
Solar Cell Production using UMG Silicon
Conference
·
Mon Sep 21 00:00:00 EDT 2009
·
OSTI ID:1176925
Limiting factors for the application of crystalline upgraded metallurgical grade silicon
Journal Article
·
Tue May 01 00:00:00 EDT 1984
· IEEE Trans. Electron Devices; (United States)
·
OSTI ID:6295700