Slurry phase Fischer-Tropsch synthesis: Cobalt plus a water-gas shift catalyst. [Quarterly] report, October 1, 1989--December 31, 1989
The rate of synthesis gas consumption over a cobalt FischerTropsch catalyst was measured in a well-mixed, continuous-flow, slurry reactor at 220 to 240{degrees}C, 0.5 to 1.5 MPa, H{sub 2}/CO feed ratios of 1.5 to 3.5 and conversions of 7 to 68% of hydrogen and 11 to 73% of carbon monoxide. The inhibiting effect of carbon monoxide was determined quantitatively and a Langmuir-Hinshelwood-type equation of the following form was found to best represent the results: -R{sub H{sub 2+Co}} = (a P{sub CO}P{sub H{sub 2}})/(1 + b P{sub CO}){sup 2}. The apparent activation energy was 93 to 95 kJ/mol. Data from previous studies on cobalt-based Fischer-Tropsch catalysts are also well correlated with this rate expression.
- Research Organization:
- Massachusetts Inst. of Tech., Cambridge, MA (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC22-87PC79816
- OSTI ID:
- 10114916
- Report Number(s):
- DOE/PC/79816--7; ON: DE93006472
- Country of Publication:
- United States
- Language:
- English
Similar Records
Slurry phase Fischer-Tropsch synthesis: Cobalt plus a water-gas shift catalyst
Slurry phase Fischer-Tropsch synthesis: Cobalt plus a water-gas shift catalyst, July 1, 1989--September 30, 1989
The hydrocarbon selectivity of cobalt Fischer-Tropsch catalysts
Technical Report
·
Sat Dec 31 23:00:00 EST 1988
·
OSTI ID:6923858
Slurry phase Fischer-Tropsch synthesis: Cobalt plus a water-gas shift catalyst, July 1, 1989--September 30, 1989
Technical Report
·
Sat Dec 31 23:00:00 EST 1988
·
OSTI ID:5062780
The hydrocarbon selectivity of cobalt Fischer-Tropsch catalysts
Technical Report
·
Mon Jul 01 00:00:00 EDT 1991
·
OSTI ID:5175068