Microporous polyimide films for reduced dielectric applications
With all the advances in the microelectronics industry, a limiting factor to computer chip speed and size is becoming the dielectric constant of the interlayer insulating materials. Dielectric constants of these layers have been reduced in going from inorganic to organic type materials. A further reduction in dielectric constant, coupled with better mechanical properties are still required for these types of materials. The authors have developed a technique involving spincoating in conjunction with a thermodynamic process called {open_quotes}Non-solvent Induced Phase Separation{close_quotes} (NSIPS) to create microporous polyimide films that exhibit both a lower dielectric constant and better stress reduction properties compared to their solid film counterparts. In this technique, the authors spincoat a soluble polyimide solution in 1,3-dimethoxybenzene solvent onto a silicon wafer, and then immediately submerse the {open_quotes}wet{close_quotes} polymer film into a non-solvent bath, typically toluene. Phase separation of the polymer occurs on a micron size scale and the resulting microporous structure becomes locked in by the high glass transition temperature of the polyimide. The authors have determined the factors affecting the film morphology, thickness, pore size, and percent porosity; these factors include the polymer concentration, spin speed, and the type of non-solvent used. The different morphologies obtained for the varying non-solvents are explained in terms of thermodynamics and kinetics of phase separation and diffusion, using an idealized ternary phase diagram. One particular film having a porosity of 68%, thickness of 22 microns and pore size of 1.4 microns had a measured dielectric constant of 1.88 and dielectric loss of 0.002. Stress measurements indicated that the microporous film reduced surface stress on the wafer by more than a factor of 10 when compared to the analogous solid polyimide film.
- Research Organization:
- Sandia National Labs., Albuquerque, NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 10106624
- Report Number(s):
- SAND-94-2831C; CONF-941142-27; ON: DE95004543; TRN: 95:000813
- Resource Relation:
- Conference: American Society of Mechanical Engineers` winter annual meeting,Chicago, IL (United States),6-11 Nov 1994; Other Information: PBD: [1995]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Engineered monodisperse mesoporous materials
Polyimide nanofoams for microelectronic applications: Nanofoams derived from 6FXDA/6FDAM-co-polypropylene oxide copolymers