The Microstructural Evolution of Inconel Alloy 740 During Solution Treatment, Aging, and Exposure at 760 °C
In this study, the microstructural evolution of Inconel alloy 740 during solution treatment and aging was characterized using optical and scanning electron microscopy. During double solution heat treatment, carbon is liberated from the dissolution of MC carbides during the first solution treatment at 1150 °C, and fine MC carbides are precipitated on gamma grain boundaries during the second solution treatment at 1120 °C. Due to the concurrent decrease in carbon solubility and the increase in the contribution of grain boundary diffusion at lower temperatures, the MC carbides on the gamma grain boundaries provide a localized carbon reservoir that aids in M23C6 carbide precipitation on gamma grain boundaries during exposure at 760 °C. The γ' phase, which is the key strengthening phase in alloy 740, is incorporated into the alloy microstructure during aging at 850 °C. Finally, the main source of microstructural instability observed during exposure at 760 °C was the coarsening of the γ' phase.
- Research Organization:
- Albany Research Center (ARC), Albany, OR (United States)
- Sponsoring Organization:
- USDOE Assistant Secretary for Energy Efficiency and Renewable Energy (EE)
- OSTI ID:
- 1010318
- Report Number(s):
- NETL-TPR-3462
- Journal Information:
- Journal of Materials Engineering and Performance, Journal Name: Journal of Materials Engineering and Performance Journal Issue: 6 Vol. 20; ISSN 1059-9495
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructural Changes in Inconel® 740 After Long-Term Aging in the Presence and Absence of Stress
A Comparison of Creep-Rupture Tested Cast Alloys HR282, IN740 and 263 for Possible Application in Advanced Ultrasupercritical Steam Turbine and Boiler