Microstructure and deformation behavior of nickel based superalloy Inconel 740 prepared by electron beam smelting
Electron beam smelting (EBS) has been used to fabricate the Inconel 740 superalloy. Microstructures, hardness, and deformation characteristics of the alloy are studied. It is observed that carbides and fine secondary phase nuclei are distributed in the hot worked EBS 740 superalloy. The Ostwald ripening occurs during solution treatment and leads to aggregation of the γ′ precipitates, the size of γ′ precipitates varies from several nanometers to more than one hundred nanometers as a result. The average size of the secondary phase is < 30 nm after aging treatment and the average Vickers hardness is measured to be about 370. The critical shear stress is calculated to be 0.627 GPa with governing mechanism of shearing, causing a stronger strengthening effect than the traditionally prepared Inconel 740 superalloy. The compression behavior indicates that the EBS 740 superalloy shows higher flow stress than 740H at low Zener-Hollomon parameter, which may arise from the undissolved γ′ precipitates and higher activation energy Q. The tensile results show that the fracture surface exhibits a ductile fracture pattern, in contrast to no obvious plastic deformation on the macroscopic fracture. Crack propagation proceeds in a transgranular fracture mode with facets and voids presented on the fracture surface. - Graphical abstract: Electron beam smelting (EBS) has been used to fabricate the Inconel 740 superalloy. Microstructures, hardness, and deformation characteristics of the alloy are studied. The average size of the secondary phase is < 30 nm after aging treatment and the average Vickers hardness is measured to be about 370. The critical shear stress is calculated to be 0.627 GPa with governing mechanism of shearing, causing a stronger strengthening effect than the traditionally prepared Inconel 740 superalloy. The EBS 740 superalloy shows higher flow stress than 740H at low Zener-Hollomon parameter, which may arise from the undissolved γ′ precipitates and higher activation energy Q. The EBS technology shows encouraging potential in preparation of nickel-based superalloys. Morphologies of γ′ precipitates and Vickers hardness as well as hot compression curves for electron beam smelting 740 superalloy. - Highlights: • Electron beam smelting, a novel method, was used to prepare the Inconel 740 superalloy. • The average size of the γ′ precipitates after aging treatment is < 30 nm. • The shearing mode generates a stronger strengthening effect than the traditional 740. • At low Zener-Hollomon parameter, the EBS 740 shows higher flow stress than 740H.
- OSTI ID:
- 22587143
- Journal Information:
- Materials Characterization, Vol. 114; Other Information: Copyright (c) 2016 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1044-5803
- Country of Publication:
- United States
- Language:
- English
Similar Records
Transition of creep damage region in dissimilar welds between Inconel 740H Ni-based superalloy and P92 ferritic/martensitic steel
An Alternative Casting Technique to Improve the Creep Resistance of Cast INCONEL Alloy 740H