Microstructure Characterization of RERTR Fuel
Conference
·
OSTI ID:940040
A variety of phases have the potential to develop in the irradiated fuels for the reduced enrichment research test reactor (RERTR) program. To study the radiation stability of these potential phases, three depleted uranium alloys were cast. The phases of interest were identified including U(Si,Al)3, (U,Mo)(Si,Al)3, UMo2Al20, UAl4, and U6Mo4Al43. These alloys were irradiated with 2.6 MeV protons at 200ºC up to 3.0 dpa. The microstructure is characterized using SEM and TEM. Microstructural characterization for an archive dispersion fuel plate (U-7Mo fuel particles in Al-2%Si cladding) was also carried out. TEM sample preparation for the irradiated dispersion fuel has been developed.
- Research Organization:
- Idaho National Lab. (INL), Idaho Falls, ID (United States)
- Sponsoring Organization:
- DOE - NE
- DOE Contract Number:
- DE-AC07-99ID-13727
- OSTI ID:
- 940040
- Report Number(s):
- INL/CON-08-14342; TRN: US0806960
- Resource Relation:
- Conference: Hot Laboratories and Remote Handling Conference (HOTLAB 2008),Kendal, UK,09/22/2008,09/23/2008
- Country of Publication:
- United States
- Language:
- English
Similar Records
Radiation Effect on Microstructural Stability of RERTR Fuel
Microstructure of RERTR DU-Alloys Irradiated with Krypton Ions
Microstructure of RERTR Du-Alloys Irradiated with Krypton Ions up to 100 dpa
Conference
·
Sat Mar 01 00:00:00 EST 2008
·
OSTI ID:940040
+2 more
Microstructure of RERTR DU-Alloys Irradiated with Krypton Ions
Conference
·
Sun Nov 01 00:00:00 EDT 2009
·
OSTI ID:940040
+4 more
Microstructure of RERTR Du-Alloys Irradiated with Krypton Ions up to 100 dpa
Journal Article
·
Fri Apr 01 00:00:00 EDT 2011
· Journal of Nuclear Materials
·
OSTI ID:940040
+4 more