Method for preparing ceramic composite
Patent
·
OSTI ID:870240
- Oak Ridge, TN
- Lenoir City, TN
- Knoxville, TN
A process for preparing ceramic composite comprising blending TiC particulates, Al.sub.2 O.sub.3 particulates and nickle aluminide and consolidating the mixture at a temperature and pressure sufficient to produce a densified ceramic composite having fracture toughness equal to or greater than 7 MPa m.sup.1/2, a hardness equal to or greater than 18 GPa.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- DOE Contract Number:
- AC05-84OR21400
- Assignee:
- Martin Marietta Energy Systems, Inc. (Oak Ridge, TN)
- Patent Number(s):
- US 5482673
- OSTI ID:
- 870240
- Country of Publication:
- United States
- Language:
- English
Similar Records
Method for preparing ceramic composite
Process for making a titanium diboride-chromium diboride-yttrium titanium oxide ceramic composition
Process for making a titanium diboride-chromium diboride-yttrium titanium oxide ceramic composition
Patent
·
Tue Jan 09 00:00:00 EST 1996
·
OSTI ID:870240
+1 more
Process for making a titanium diboride-chromium diboride-yttrium titanium oxide ceramic composition
Patent
·
Wed Jan 01 00:00:00 EST 1992
·
OSTI ID:870240
Process for making a titanium diboride-chromium diboride-yttrium titanium oxide ceramic composition
Patent
·
Tue Apr 28 00:00:00 EDT 1992
·
OSTI ID:870240
Related Subjects
method
preparing
ceramic
composite
process
comprising
blending
tic
particulates
nickle
aluminide
consolidating
mixture
temperature
pressure
sufficient
produce
densified
fracture
toughness
equal
mpa
hardness
18
gpa
ceramic composite
fracture toughness
composite comprising
pressure sufficient
preparing ceramic
densified ceramic
/419/75/
preparing
ceramic
composite
process
comprising
blending
tic
particulates
nickle
aluminide
consolidating
mixture
temperature
pressure
sufficient
produce
densified
fracture
toughness
equal
mpa
hardness
18
gpa
ceramic composite
fracture toughness
composite comprising
pressure sufficient
preparing ceramic
densified ceramic
/419/75/