Synthesis of iron based hydrocracking catalysts
Patent
·
OSTI ID:868793
- Pittsburgh, PA
- Barboursville, VA
A method of preparing a fine particle iron based hydrocracking catalyst and the catalyst prepared thereby. An iron (III) oxide powder and elemental sulfur are reacted with a liquid hydrogen donor having a hydroaromatic structure present in the range of from about 5 to about 50 times the weight of iron (III) oxide at a temperature in the range of from about 180.degree. C. to about 240.degree. C. for a time in the range of from about 0 to about 8 hours. Various specific hydrogen donors are disclosed. The catalysts are active at low temperature (<350.degree. C.) and low pressure.
- Research Organization:
- National Energy Technology Laboratory (NETL), Pittsburgh, PA, Morgantown, WV (United States); USDOE Pittsburgh Energy Technology Center (PETC), PA (United States)
- Assignee:
- United States of America as represented by United States (Washington, DC)
- Patent Number(s):
- US 5214015
- OSTI ID:
- 868793
- Country of Publication:
- United States
- Language:
- English
Finely dispersed iron, iron-molybdenum, and sulfated iron oxides as catalysts for coprocessing reactions
|
journal | September 1991 |
Catalysis in direct coal liquefaction by sulfated metal oxides
|
journal | May 1991 |
Iron compounds and iron catalysts: Activity in reactions relevant to direct coal liquefaction
|
journal | December 1991 |
Catalytic roles of iron and hydrogen sulphide on hydrogenation of coal
|
journal | May 1984 |
Similar Records
Synthesis of iron based hydrocracking catalysts
Synthesis of iron based hydrocracking catalysts
Method for preparing a promoted iron catalyst and catalyst prepared by the method for conversion of synthesis gas to liquid hydrocarbons
Patent
·
Tue May 25 00:00:00 EDT 1993
·
OSTI ID:868793
Synthesis of iron based hydrocracking catalysts
Patent Application
·
Thu Dec 31 00:00:00 EST 1992
·
OSTI ID:868793
Method for preparing a promoted iron catalyst and catalyst prepared by the method for conversion of synthesis gas to liquid hydrocarbons
Patent
·
Tue Feb 19 00:00:00 EST 1991
·
OSTI ID:868793
Related Subjects
synthesis
iron
based
hydrocracking
catalysts
method
preparing
fine
particle
catalyst
prepared
iii
oxide
powder
elemental
sulfur
reacted
liquid
hydrogen
donor
hydroaromatic
structure
range
50
times
weight
temperature
180
degree
240
time
hours
various
specific
donors
disclosed
active
350
pressure
iron based
hydrogen donor
elemental sulfur
oxide powder
liquid hydrogen
fine particle
cracking catalyst
catalyst prepared
hydrocracking catalyst
particle iron
based hydrocracking
iron base
/502/
iron
based
hydrocracking
catalysts
method
preparing
fine
particle
catalyst
prepared
iii
oxide
powder
elemental
sulfur
reacted
liquid
hydrogen
donor
hydroaromatic
structure
range
50
times
weight
temperature
180
degree
240
time
hours
various
specific
donors
disclosed
active
350
pressure
iron based
hydrogen donor
elemental sulfur
oxide powder
liquid hydrogen
fine particle
cracking catalyst
catalyst prepared
hydrocracking catalyst
particle iron
based hydrocracking
iron base
/502/