Ductile tungsten-nickel-alloy and method for manufacturing same
Patent
·
OSTI ID:863088
- Kingston, TN
The tensile elongation of a tungsten-nickel-iron alloy containing essentially 95 weight percent reprocessed tungsten, 3.5 weight percent nickel, and 1.5 weight percent iron is increased from a value of less than about 1 percent up to about 23 percent by the addition of less than 0.5 weight percent of a reactive metal consisting of niobium and zirconium.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- DOE Contract Number:
- W-7405-ENG-26
- Assignee:
- United States of America as represented by Department of Energy (Washington, DC)
- Patent Number(s):
- US 4090875
- OSTI ID:
- 863088
- Country of Publication:
- United States
- Language:
- English
Similar Records
Ductile tungsten--nickel-alloy and method for manufacturing same
Ductile tungsten-nickel alloy and method for making same
Development of ductile tungsten alloys
Patent
·
Tue May 23 00:00:00 EDT 1978
·
OSTI ID:863088
Ductile tungsten-nickel alloy and method for making same
Patent
·
Thu Jan 01 00:00:00 EST 1976
·
OSTI ID:863088
Development of ductile tungsten alloys
Technical Report
·
Thu Aug 03 00:00:00 EDT 1961
·
OSTI ID:863088
+1 more
Related Subjects
ductile
tungsten-nickel-alloy
method
manufacturing
tensile
elongation
tungsten-nickel-iron
alloy
containing
essentially
95
weight
percent
reprocessed
tungsten
nickel
iron
increased
value
23
addition
reactive
metal
consisting
niobium
zirconium
tungsten-nickel-iron alloy
alloy containing
active metal
weight percent
reactive metal
metal consisting
percent nickel
percent iron
tensile elongation
iron alloy
containing essentially
/75/419/420/
tungsten-nickel-alloy
method
manufacturing
tensile
elongation
tungsten-nickel-iron
alloy
containing
essentially
95
weight
percent
reprocessed
tungsten
nickel
iron
increased
value
23
addition
reactive
metal
consisting
niobium
zirconium
tungsten-nickel-iron alloy
alloy containing
active metal
weight percent
reactive metal
metal consisting
percent nickel
percent iron
tensile elongation
iron alloy
containing essentially
/75/419/420/